Modulated structures in Ni-Al and Fe-Ni-Al-C alloysNi-Al과 Fe-Ni-Al-C 계 합금의 MODULATED 구조

Cited 0 time in webofscience Cited 0 time in scopus
  • Hit : 418
  • Download : 0
The primary goal of this thesis is to investigate the modulated structures found in Ni-rich Ni-Al and austenitic Fe-Ni-Al-C alloys. Ordering and clustering in rapidly-solidified Ni-14\% Al have been analyzed by transmission electron microscopy and X-ray diffraction investigation. To examine the formation processes of $\gamma\,``$ phase($L1_2$ structure), the disordered state of starting specimen was sought through the rapid solidification process by melt spinning. In the highly undercooled condition, the supersaturated $\gamma$ follows its characteristic mode of $Ll_2$ ordering/clustering with respect to experimental variables. At relatively low temperature($500\,^\circ\!C$), $\gamma$ firstly goes through continuous ordering and subsequently undergoes phase separation. While at intermediate ageing temperature($710\,^\circ\!C$), $\gamma\,``$ phase precipitates via the nucleation and gorwth mechanism. At this temperature, the morphology of $\gamma\,``$ precipitates evolves as follows:quasi-randomly distributed cuboids $\rightarrow$ rows of cubic particles $\rightarrow$ plates. gowth kinetics of $\gamma\,``$ particles obeys the LSW (Lifshitz, Slyozov and Wagner) theory. Such a coupled ordering/clustering phenomenon fairly well is explained qualitatively by the metastable phase diagram subdivided by the loci of $T_i$+(disordering instability), $T_o$ (critical ordering), $T_i$-(ordering instability) and Ts(spinodal instability) temperatures. The phase decomposition of Fe-42.4wt\% Ni-4.15wt\% Al-0.45wt\% C alloy was investigated on ageing at 823K by means of micrographs, selected area diffraction patterns, micro-beam diffraction patterns and microprobe chemical analyses obtained by conventional transmission electron microscopy and scanning transmission electron microscopy. In the matrix, the K phase with $L``1_2$ structure has formed via the zone formation process. This matrix perovskite carbide is gradually repslaced by the discontinuously precipitated grain boundar...
Advisors
Choo, Woong-Kil추웅길
Description
한국과학기술원 : 재료공학과,
Publisher
한국과학기술원
Issue Date
1991
Identifier
61819/325007 / 000855312
Language
eng
Description

학위논문(박사) - 한국과학기술원 : 재료공학과, 1991.2, [ [vi], 110 p. ]

URI
http://hdl.handle.net/10203/50079
Link
http://library.kaist.ac.kr/search/detail/view.do?bibCtrlNo=61819&flag=dissertation
Appears in Collection
MS-Theses_Ph.D.(박사논문)
Files in This Item
There are no files associated with this item.

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0