Título: | Estudio calorimétrico no isotérmico del proceso de precipitación en una aleación de Cu-10 % Ni-3 % Al |
Otros títulos: | Non isothermal calorimetric study of the precipitation processes in a Cu-10% Ni-3% Al alloy | Autor: | Donoso, E.; Diánez, M.J. CSIC ORCID; Sayagués, María Jesús CSIC ORCID; Criado Luque, J.M. CSIC; Varschavsky, A.; Díaz, G. | Palabras clave: | DSC Precipitación Cobre Cu-Ni-Al Microdureza Cinética Precipitation Copper Microhardness Kinetics |
Fecha de publicación: | 30-abr-2007 | Editor: | Consejo Superior de Investigaciones Científicas (España) | Citación: | Revista de Metalurgia 43(2): 117-124 (2007) | Resumen: | [ES] Mediante calorimetría diferencial de barrido (DSC), se estudió el proceso de precipitación de
átomos de níquel y aluminio a partir de una solución sólida de Cu-Ni-Al. El análisis de las
curvas calorimétricas muestra la presencia de dos reacciones exotérmicas (etapas 1 y 2),
que se interpretan como la formación de dos tipos de precipitados. La primera etapa corresponde
a la formación de la fase de equilibrio b (NiAl), en tanto que la etapa 2 corresponde
a la formación del precipitado g’ de composición estequiométrica Ni3Al. Además, se observa
que las curvas se desplazan a temperaturas más bajas a medida que la velocidad de
calentamiento lineal decrece. Las energías de activación de las reacciones fueron evaluadas
a partir de un método de Kissinger modificado. Los parámetros cinéticos se calcularon
mediante el formalismo de Johnson- Mehl-Avrami. Los valores de n obtenidos son indicativos
de un proceso de nucleación de partículas a partir de núcleos pre existentes. Las medidas
de microdureza y las micrografías obtenidas por microscopía electrónica de transmisión
ayudaron a confirmar la formación de las fases antes indicadas. [EN] Using differential scanning calorimetry (DSC), the precipitation process of nickel and aluminium atoms from a solid solution of Cu-Ni-Al were studied. Analysis of calorimetric traces displayed shows the presence of two exothermic reactions (stage 1 and 2), which were interpreted as the formation of two types of precipitates. The first stage corresponds to the formation of an equilibrium b (NiAl) phase, whilst stage 2 corresponds to the formation of g’ precipitate with Ni3Al stoichiometric composition. It is observed the shift of the traces to lower temperatures while linear heating rate decrease. The activation reaction energies were evaluated from modified Kissinger’s method. Kinetic parameters were calculated by means Johnson-Mehl-Avrami formalism. The values obtained for parameter n were indicative of a particle nucleation process from pre-existent nucleus. Microhardness measurements and micrographies obtained by transmission electron microscopy were helpful to confirm the formation and the dissolution of the mentioned phases. |
Descripción: | 8 páginas, 6 figuras, 2 tablas. | Versión del editor: | http://dx.doi.org/10.3989/revmetalm.2007.v43.i2.58 | URI: | http://hdl.handle.net/10261/21123 | DOI: | 10.3989/revmetalm.2007.v43.i2.58 | ISSN: | 0034-8570 | E-ISSN: | 1988-4222 |
Aparece en las colecciones: | (ICMS) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
58.pdf | 1,49 MB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
6
checked on 23-abr-2024
Page view(s)
471
checked on 23-abr-2024
Download(s)
206
checked on 23-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.