Effect of solvent type on coating film formation

0101304 - UMCH-V 20043024 RIV FR eng C - Konferenční příspěvek (zahraniční konf.)
Vlasák, P. - Dušková-Smrčková, Miroslava - Dušek, Karel
Effect of solvent type on coating film formation.
[Vliv typu rozpouštědla na tvorbu nátěrového filmu.]
Congress Proceedings. Paris: French Association of Technicians of Paints, Varnishes, Inks and Adhesives, 2004, s. 1119-1123. 3.
[FATIPEC Congress /27./. Aix-en-Provence (FR), 19.04.2004-21.04.2004]
Grant CEP: GA ČR GA104/03/1378
Výzkumný záměr: CEZ:AV0Z4050913
Klíčová slova: coating film * solvent entrapment * isocyanate
Kód oboru RIV: CD - Makromolekulární chemie

In the formation process of solvent-born crosslinked coating films, solvent type plays an important role. Four isomers of butyl acetate were used as film-forming solvents for two-component polyurethane coatings. The rate of evaporation, solvent retention, film drying time and hardness development were determined. Tertiary butyl acetate, the most volatile solvent, promotes fast drying but the film hardness is the worst. This is caused by the highest solvent retention.

Tvorba síťovaného filmu závisí silně na typu rozpouštědla použitého v příslušné nátěrové hmotě. Čtyři izomery butylacetátu byly použity jako filmotvorná rozpouštědla dvousložkového polyurethanového nátěru. Nejtěkavější terciární butyl acetát podporuje rychlé zasychání, ale tvrdost vzniklého filmu je nejhorší v důsledku nejvyšší zádrže rozpouštědla.