Ce.sup.3+./sup. luminescence in a LiBaF.sub.3./sub. single crystal at low temperature

0133967 - FZU-D 20020255 RIV US eng J - Článek v odborném periodiku
Nikl, Martin - Mihóková, Eva - Málková, Zuzana - Vedda, A. - Martini, M. - Shimamura, K. - Fukuda, T.
Ce³⁺ luminescence in a LiBaF₃ single crystal at low temperature.
[Ce3+ luminescence v monokrystalu LiBaF3 za nízkých teplot.]
Physical Review. B. Roč. 66, - (2002), s. 184101-1. ISSN 0163-1829
Grant CEP: GA MŠMT ME 519
Výzkumný záměr: CEZ:AV0Z1010914
Klíčová slova: LiBaF₃:Ce * luminescence * decay kinetics
Kód oboru RIV: BM - Fyzika pevných látek a magnetismus
Impakt faktor: 3.327, rok: 2002

The luminescence and decay kinetics of Ce ³⁺-based centers in a LiBaF₃ single crystal are reported in the 80-300 K temperature range. At about 130 K the leading low-temperature double-peak emission band at 270/296 nm is transformed into a single peak at 325 nm. The information is also well reflected in the decay kinetics of both emission bands.

Luminiscence a kinetika dosvitu center na bázi Ce3+ v monokrystalu LiBaF3 v oblasti teplot 80-300 K je předmětem této práce. Při cca 130 K je dominantní dvojitý emisní pík u 270/296 nm transformován v jednoduchý pík u 325 nm. Tato transformace je dobře patrná take v kinetice dosvitu obou pásů. Jednoduchý dvouhladinový model s teplotní bariérou je použit k aproximaci experimentálních dat. Vysvětlení pozorovaných charakteristik je na bázi dynamické výměny iontů Li a Ba v nejblžším okolí excitovaného iontu Ce3+. Termoluminiscenční charakteristiky za nízkých teplot podporují možnost takové nestability v mříži LiBaF3