Effect of cooling rate on glass transition temperature and enthalpy and volume relaxation of polystyrene

0053675 - ÚH 2007 RIV JP eng C - Konferenční příspěvek (zahraniční konf.)
Slobodian, P. - Hadač, J. - Říha, Pavel - Sáha, P. - Kubát, J.
Effect of cooling rate on glass transition temperature and enthalpy and volume relaxation of polystyrene.
[Vliv rychlosti chlazení na teplotu skelného přechodu a relaxaci entalpie a objemu polystyrénu.]
22nd Annual Meeting of the Polymer Processing Society. Yamagata: PPS, 2006, G07.03. ISBN 4-9903109-1-8.
[Annual Meeting of the Polymer Processing Society /22./. Yamagata (JP), 02.07.2006-06.07.2006]
Grant CEP: GA ČR GA103/05/0803
Výzkumný záměr: CEZ:AV0Z20600510
Klíčová slova: Enthalpy relaxation * Glass transition * Polystyrene
Kód oboru RIV: BJ - Termodynamika

Cooling rate dependence of glass transition temperature was measured for polystyrene using mercury-in-glass dilatometry. The enthalpy (DSC apparatus) and volume relaxation of polystyrene were measured after cooling from equilibrium liquid state to relaxation temperature below Tg after cooling by different rate. Enthalpy and volume relaxation data were discussed in terms of Kohlrauch-Williams-Watt expression. From enthalpy and volume relaxation data the ratio enthalpy/volume was calculated giving 1.8 GPa, similar to the bulk modulus measured by direct compression.

Byla měřena závislost hodnoty teploty skelného přechodu Tg na rychlosti chlazení pomocí mercury-in-glass dilatometrie. Relaxace entalpie (DSC přístroj) a objemu polystyrenu byla měřena z rovnovážného stavu nad Tg do teploty pod teplotou skelného přechodu při různých rychlostech chlazení. Relaxace entalpie a objemu byla popsána rovnicí Kohlrauch-Williams-Watt. Z experimentálních dat byl určen poměr entalpie/objem dávající hodnotu 1.8 GPa která je blízká hodnotě objemového modulu měřeného přímou kompresí.