Computational estimation of micro-crack behaviour in polypropylene copolymer

0318819 - ÚFM 2009 ES eng A - Abstrakt
Hutař, Pavel - Majer, Zdeněk - Knésl, Zdeněk - Náhlík, Luboš - Šestáková, Lucie - Prod’homme, G.
Computational estimation of micro-crack behaviour in polypropylene copolymer.
[Výpočetní odhad chování mikrotrhliny v polypropylenovém kopolymeru.]
WCCM8 ECCOMAS 2008. Barcelona: CIMNE, 2008. s. 1-2.
[World Congress on Computational Mechanics. 30.06.2008-04.07.2008, Venice]
Grant CEP: GA AV ČR(CZ) KJB200410803; GA AV ČR 1QS200410502; GA ČR GA106/07/1284
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: multiscale modelling * fracture mechanics * representative unit cell * microcracks
Kód oboru RIV: JL - Únava materiálu a lomová mechanika

Polymeric particulate composites are frequently used in many engineering applications. The composite was modeled as a three-phase continuum-matrix, interphase and particle. The presence of particles significantly influences the cure reaction, resulting in the formation of the third phase known as the interphase, which possess property distinct from those of the matrix and the particle. Computation of the internal stress and strain fields in the micro-structural level of the studied composite and understanding of micro-cracks behaviour in the interaction with particles is the first step to understanding the global behaviour of the composite based on micro-structural morphology. Therefore, particle reinforced composite has been modelled as a three-phase material with homogenously distributed coated particles and numerically studied on the microscopic scale using finite element modelling.

V dnešní době se stále častěji využívají kompozitní materiály. Tato práce je zaměřena na studium vlivu přítomnosti částice v polymerní matrici. Přidáním částic dochází ke vzniku další třetí fáze - mezifáze. Ta může výrazně ovlivnit lomově-mechanické chování kompozitu jako celku.