THE EFFECT OF THRESHOLD VALUE ON THE RESIDUAL FATIGUE LIFETIME OF RAILWAY AXLES
- 1.0434943 - ÚFM 2015 RIV CZ eng C - Konferenční příspěvek (zahraniční konf.)
Pokorný, Pavel - Náhlík, Luboš - Hutař, Pavel
THE EFFECT OF THRESHOLD VALUE ON THE RESIDUAL FATIGUE LIFETIME OF RAILWAY AXLES.
Engineering mechanics 2014. Brno: Brno University of Technology, 2014 - (Fuis, V.), s. 496-499. ISBN 978-80-214-4871-1. ISSN 1805-8248.
[Engineering Mechanics 2014 /20./. Svratka (CZ), 12.05.2014-15.05.2014]
Grant CEP: GA MŠMT(CZ) EE2.3.20.0214
Institucionální podpora: RVO:68081723
Klíčová slova: railway axle * threshold value * fatigue crack * residual fatigue lifetim
Kód oboru RIV: JL - Únava materiálu a lomová mechanika
The fatigue failure of railway axles could have unaccepted consequences. Because of safe operation, it is important to determine the residual fatigue lifetime. The railway axle could contain some cracks either from manufacturing process or from previous service operation. Present defectoscopy can reliably detect only relatively long cracks (longer than 2 mm), see [1]. In other words, there is a risk that the existing crack is not detected by defectoscopy. For conservative establishment of the residual fatigue lifetime the crack, which could be not detected by defectoscopy, must be considered. This paper deals with an effect of the threshold value of fatigue crack propagation on the residual fatigue lifetime of railway axles. Two very commonly used materials for railway axles EA1N and EA4T steels are considered. The results of this paper could be used for safer operation of railway axles.