Influence of Inorganic Bases on the Structure of Titanium Dioxide-Based Microsheets

  1. 1.
    0532239 - ÚACH 2021 RIV US eng J - Článek v odborném periodiku
    Svora, Petr - Ecorchard, Petra - Pližingrová, Eva - Komárková, Bára - Svorová Pawełkowicz, Sylwia - Murafa, Nataliya - Maříková, Monika - Smržová, Darina - Wagner, B. - Machálková, Aneta - Bezdička, Petr
    Influence of Inorganic Bases on the Structure of Titanium Dioxide-Based Microsheets.
    ACS Omega. Roč. 5, č. 37 (2020), s. 23703-23717. ISSN 2470-1343. E-ISSN 2470-1343
    Grant CEP: GA ČR(CZ) GA18-26297S; GA MŠMT(CZ) LM2018124
    Institucionální podpora: RVO:61388980
    Klíčová slova: Oxides * Anions * Minerals * Oscillation
    Obor OECD: Inorganic and nuclear chemistry
    Impakt faktor: 3.512, rok: 2020
    Způsob publikování: Open access

    Laboratory synthesis of microsheets of titanium dioxide from titanyl sulfate involves the use of ammonia solution, whereas another inorganic base is most likely to be employed at the industrial level, as ammonia is a toxic agent and therefore should be avoided according to European Union (EU) regulations. Selected nontoxic bases such as sodium, potassium, and lithium hydroxides have been tested as an alternative to ammonia solution to obtain amorphous and crystalline TiO2-based microsheets. The final products obtained at each step of the procedure (samples lyophilized and annealed at 230 and 800 °C) were analyzed with electron and atomic force microscopy, X-ray powder diffraction, thermal analysis, and Fourier transform infrared (FTIR) and Raman spectroscopies to determine their morphology and phase composition. The differences in the morphology of the obtained products were described in detail as well as phase and structural composition throughout the process. It was found that, in the last step of the synthesis, microsheets annealed at 800 °C were built of small rods and oval or platy crystalline particles depending on the base used. The temperature of formation of anatase, rutile, and alkali-metal titanates in correlation with the ionic radius of the alkali metal present in the sample was discussed.
    Trvalý link: http://hdl.handle.net/11104/0311764

     
    Název souboruStaženoVelikostKomentářVerzePřístup
    Influence.pdf15.5 MBCC-BY-NC-ND licenceAutorský postprintpovolen
    Influence SI.pdf22 MBCC-BY-NC-ND licenceVydavatelský postprintvyžádat
     
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.