Rheological and erosion studies regarding a liposome-containing polymeric blend that is propaedeutic to its use in paving techniques in tubular organs, such as blood vessels, are reported. Attention is focused on an aqueous polymeric blend composed of Pluronic (PF127) and alginate (Protanal LF 10/60) because both polymers, when dissolved in water at a sufficiently high concentration, are subjected to different structural mechanisms, which are driven by temperature increase and addition of bivalent cations, respectively, and both result in marked viscoelastic and plastic properties. After proving the compatibility between PF127 and alginate, we show that the structural transition temperature of the blend, TST, can be properly modulated. In particular, we found that TST for an aqueous solution of pure Pluronic 20% w/w is about 21 ◦C and that even slight reductions in polymer concentration result in considerable TST decrease. The addition of salts or alginate (provided as Na-alginate) provokes a substantial decrease of TST and thus the alginate concentration in the blend should not exceed 1% w/w. In addition, liposomes slow down the structural transition but do not substantially affect the rheological properties of the system in the final state at higher temperatures, thus showing that they can be added to the polymeric blend without significant effects. Finally, erosion tests show that after contact with a source of bivalent cations, the polymeric blend containing PF127 and alginate shows an erosion resistance neatly improved with respect to the simple structured Pluronic system having the same polymer concentration. As a whole, all these results constitute the basis for future potential applications of the considered polymeric blend in tubular organs such as blood vessels.

Rheological properties of aqueous Pluronic-alginate systems containing liposomes

Grassi G.;CREVATIN, ANDREA;Farra R.;Guarnieri G.;PASCOTTO, ANDREA SANTE;Lapasin R.;Grassi M.
2006-01-01

Abstract

Rheological and erosion studies regarding a liposome-containing polymeric blend that is propaedeutic to its use in paving techniques in tubular organs, such as blood vessels, are reported. Attention is focused on an aqueous polymeric blend composed of Pluronic (PF127) and alginate (Protanal LF 10/60) because both polymers, when dissolved in water at a sufficiently high concentration, are subjected to different structural mechanisms, which are driven by temperature increase and addition of bivalent cations, respectively, and both result in marked viscoelastic and plastic properties. After proving the compatibility between PF127 and alginate, we show that the structural transition temperature of the blend, TST, can be properly modulated. In particular, we found that TST for an aqueous solution of pure Pluronic 20% w/w is about 21 ◦C and that even slight reductions in polymer concentration result in considerable TST decrease. The addition of salts or alginate (provided as Na-alginate) provokes a substantial decrease of TST and thus the alginate concentration in the blend should not exceed 1% w/w. In addition, liposomes slow down the structural transition but do not substantially affect the rheological properties of the system in the final state at higher temperatures, thus showing that they can be added to the polymeric blend without significant effects. Finally, erosion tests show that after contact with a source of bivalent cations, the polymeric blend containing PF127 and alginate shows an erosion resistance neatly improved with respect to the simple structured Pluronic system having the same polymer concentration. As a whole, all these results constitute the basis for future potential applications of the considered polymeric blend in tubular organs such as blood vessels.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11368/2946699
 Avviso

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? 8
  • Scopus 60
  • ???jsp.display-item.citation.isi??? 54
social impact