Monitoring of 13% Cr martensitic stainless steel corrosion in chloride solution in presence of thiosulphate by acoustic emission technique

Corrosion behaviour under tensile load of 13% Cr martensitic stainless steel in an acidified chloride solution in presence of thiosulphate ions (10−2 M) was evaluated by acoustic emission (AE) technique. AE source localization along specimen length allowed to identify different damage mechanisms characterized by specific AE parameters. Few large pits have been observed on specimen surface. Pit growth mechanism changed during time. All specimens failed after about 300–400 h by cracks originated at a pit tip. Cracks started to propagate in a cleavage microductile mode and then propagate in a brittle intergranular mode. Final rupture was characterized by ductile propagation.