The elastic constants of yttria stabilised-zirconia coatings produced by a recently developed Low Pressure Plasma Spraying system were measured by in-situ diffraction in a four- point bending device. The anisotropic nature of the cubic zirconia coatings was investigated by collecting diffraction data under increasing load along two crystallographic directions ([440] and [620]). The four point bending was such to add compression to the measured coating surface, in order to progressively increase the compressive (residual) stress already present in the material. Unlike conventional Plasma Spray ceramic coatings, the elastic constants and the anisotropy of the studied LPPS coatings are comparable with those of the corresponding bulk materials. Average compressive residual stress in excess of –500 MPa was found in ~24 µm thick coatings.

Elastic constants of LPPS stabilized-zirconia coatings

Leoni, Matteo;Scardi, Paolo;
2002-01-01

Abstract

The elastic constants of yttria stabilised-zirconia coatings produced by a recently developed Low Pressure Plasma Spraying system were measured by in-situ diffraction in a four- point bending device. The anisotropic nature of the cubic zirconia coatings was investigated by collecting diffraction data under increasing load along two crystallographic directions ([440] and [620]). The four point bending was such to add compression to the measured coating surface, in order to progressively increase the compressive (residual) stress already present in the material. Unlike conventional Plasma Spray ceramic coatings, the elastic constants and the anisotropy of the studied LPPS coatings are comparable with those of the corresponding bulk materials. Average compressive residual stress in excess of –500 MPa was found in ~24 µm thick coatings.
2002
Residual Stresses VI, ECRS6
Svizzera
TTP Trans Tech Publications
0878499008
9780878499007
Leoni, Matteo; Scardi, Paolo; M., Loch; G., Barbezat
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11572/73596
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 0
  • ???jsp.display-item.citation.isi??? 0
social impact