Mechanical behavior of dip-brazed aluminum sandwich panels
Citable URI: http://hdl.handle.net/1721.1/38585
| Title: | Mechanical behavior of dip-brazed aluminum sandwich panels |
| Author: | Hohmann, Brian P. (Brian Patrick) |
| Advisor: | Thomas W. Eagar. |
| Department: | Massachusetts Institute of Technology. Dept. of Materials Science and Engineering. |
| Abstract: |
An experimental study was carried out to determine the mechanical behavior of sandwich panels containing cellular cores of varying shape. Compression and four point bend tests were performed on sandwich panels with square and triangular honeycomb cores. These honeycombs were made of perforated aluminum sheet of repeating diamond and hexagonal patterns. The sandwich panel assemblies were joined via dip brazing. Defects were introduced into some panels to quantify the effect on strength and stiffness. Hybrid sandwich panels, consisting of foam material in the void spaces of the square and triangular cells were evaluated for the effect on the defect tolerance of the structures. The results showed that sandwich panels with diamond shaped cores had compressive strengths approximately four times greater than hexagonal shaped cores. In four point bending the diamond cores were approximately twice as stiff as cores made from hexagonal patterned sheet. The introduction of defects lowered strength by about 30% for diamond cores in compression, and about 15% for hexagonal cores. In four point bending this strength reduction was not as significant due to shear stresses damaging periodicity at a faster rate than in compression. (cont.) The use of foam within the cells resulted in higher absolute peak compression and flexure loads, however the Load/Density ratios demonstrated cases where the added weight of the foam did not result in a better panel. A difference of nearly an order of magnitude between the highest and lowest compressive and flexure loads is evident when the presence of defects and foam are taken into account. |
| Description: | Thesis (S.M.)--Massachusetts Institute of Technology, Dept. of Materials Science and Engineering, 2007. "February 2007." Vita. Includes bibliographical references (leaves 158-160). |
| URI: | http://hdl.handle.net/1721.1/38585 |
| Issue Date: | 2007 |
| Publisher: | Massachusetts Institute of Technology |
| Keywords: | Materials Science and Engineering. |
Files in this item
| Files | Size | Format |
|---|---|---|
| Preview, non-printable (open to all) | 6.859Mb | application/pdf |
| Full printable version (MIT only) | 6.859Mb | application/pdf |
This item appears in the following Collection(s)
All Items in DSpace@MIT are protected by original copyright, with all rights reserved, unless otherwise indicated.
|
|
Contact
MIT Libraries
|