New RTM/RI Resins for the HSCTIn the first portion of this work, 1,2,3,3,4,4-hexafluoro-1,2-bis[4-(dimethylhydroxysilyl)phenoxy]cyclobutane and 1,2,3,3,4,4-hexafluoro-1,2-bis[3-(dimethylhydroxysilyl)phenoxy]cyclobutane were prepared and homopolymerized to afford polymers with excellent thermal stability and Tgs of 27 C and -12 C, respectively. Despite the moderately high wt% of fluorin in the polymer structure (23.8%), these polymers had poor fuel resistance. In fact, swelling measurements indicate that these polymers had apparent solubility parameters of about 18.2 J (exp 1/2) m (exp -3/2) (toluene). Copolymerization of the disilanol monomers with fluorosilicone monomers afforded copolymers containing 20-30 wt% of the perfluorocyclobutane-containing structure displayed adequate fuel resistance, enhanced thermal stability, and a Tg low enough to meet the requirements of a High Speed Civil Transport (HSCT) fuel tank sealant. In the second part of this work, trifluorovinylether-terminated oligomers were prepared and polymerized via cyclodimerization. Initially, an alpha, omega-silanol-terminated fluorosilicone was endcapped with trifluorovinylether end groups via a two-step synthetic sequence. The oligomer was thermally cyclodimerized to a polymer that displayed thermal stability similar to that of a fluorosilicone homopolymer. Second, 1,3-bis[4-trifluorovinyl(oxy)phenyl]-1,3-(3,3,3-trifluoropropyl)dimethyldisiloxane and 1,3-bis{3-trifluorovinyl(oxy)phenyl]-1,3-(3,3,3-trifluoropropyl)dimethyldisiloxane were prepared and cyclodimerized to afford polymers that contained pendant trifluoropropyl groups. The pendant trifluoropropyl groups did enhance solvent resistance in aliphatic hydrocarbon solvents, however, no improvement was observed in aromatic hydrocarbon solvents. These polymers also displayed excellent thermal stability. In the last part of this work, a series of monomers was prepared by the DCC-promoted esterification of 4-[trifluorovinyl(oxy)benzoic acid with alpha, omega-functionalized hydrogenated and partially fluorinated alcohols. The monomers were cyclodimerized to the corresponding polymers. The polymers that did not contain beta hydrogens displayed significantly higher thermal stability than the fully hydrogenated polymers. A commercially-available alpha,omega-hydroxy-terminated perfluoropolyether was then functionalized with 4-[trifluorovinyl(oxy)benzoylchloride. An attempt was made to polymerize the resulting oligomer via the cyclodimerization of the terminal trifluorovinylether moieties. Although the viscosity of the oligomer increased significantly during polymerization, Gel Permeation Chromatography (GPC) analysis revealed that the Tetrahydrofuran (THF) soluble portion of the polymer did not have high molecular weight.
Document ID
19990116374
Acquisition Source
Langley Research Center
Document Type
Other
Authors
Harris, Frank W. (Akron Univ. Akron, OH United States)
Date Acquired
September 6, 2013
Publication Date
October 1, 1999
Subject Category
Nonmetallic Materials
Funding Number(s)
CONTRACT_GRANT: NAG1-2067
Distribution Limits
Public
Copyright
Work of the US Gov. Public Use Permitted.

Related Records

There are no records associated with this record.
No Preview Available