The post-yield fracture of a ductile polymer film: Notch quality, essential work of fracture, crack tip opening displacement, and J-integral
Visualitza/Obre
10.1016/j.engfracmech.2017.01.019
Inclou dades d'ús des de 2022
Cita com:
hdl:2117/100684
Tipus de documentArticle
Data publicació2017
Condicions d'accésAccés obert
Llevat que s'hi indiqui el contrari, els
continguts d'aquesta obra estan subjectes a la llicència de Creative Commons
:
Reconeixement-NoComercial-SenseObraDerivada 3.0 Espanya
Abstract
Double edge notched tension (DENT) specimens of a polyethylene terephthalate (PET) film were tested in an universal testing machine, measuring the displacements and the ligament lengths with a digital image correlation (DIC) system. With these data the essential work of fracture (EWF), crack tip opening displacement (CTOD), and the J-integral fracture methods were compared. The specimens were tested in mode I under plane stress conditions, verifying that the crack always propagated through a fully yielded ligament. It has been proved that we, the specific essential work of fracture was the specific energy just up to crack initiation and has the same value that J-integral at crack initiation, Jo. The relationship of these parameters with the CTOD was also shown. The influence of the notch quality on the fracture behaviour when the specimens were sharpened by two different methods, femtosecond laser ablation or by razor blade sliding, has also been analysed in detai
CitacióMartinez, A., Leon, N., Arencon, D., Sanchez-Soto, M. The post-yield fracture of a ductile polymer film: Notch quality, essential work of fracture, crack tip opening displacement, and J-integral. "Engineering fracture mechanics", 2017, vol. 173, p. 21-31.
ISSN0013-7944
Versió de l'editorhttp://www.sciencedirect.com/science/article/pii/S0013794416303897
Fitxers | Descripció | Mida | Format | Visualitza |
---|---|---|---|---|
EFM_5383_edit_report-1.pdf | Article pre-print | 1,056Mb | Visualitza/Obre |