Characterization, integration and reliability of HfO$_2$ and LaLuO$_3$ high-$\kappa$/metal gate stacks for CMOS applications



2013
Forschungszentrum Jülich GmbH Zentralbibliothek, Verlag Jülich
ISBN: 978-3-89336-898-3

Jülich : Forschungszentrum Jülich GmbH Zentralbibliothek, Verlag, Schriften des Forschungszetrum Jülich. Reihe Information / information 28, 177 S. () = RWTH Aachen, Diss., 2013

Please use a persistent id in citations:  

Abstract: The continued downscaling of MOSFET dimensions requires an equivalent oxide thickness (EOT) of the gate stack below 1 nm. An EOT below 1.4 nm is hereby enabled by the use of high-$\kappa$/metal gate stacks. LaLuO$_{3}$ and HfO$_{2}$ are investigated as two different high-$\kappa$ oxides on silicon in conjunction with TiN as the metal electrode. LaLuO$_{3}$ and its temperature-dependent silicate formation are characterized by hard X-ray photoemission spectroscopy (HAXPES). The effective attenuation length of LaLuO$_{3}$ is determined between 7 and 13 keV to enable future interface and diffusion studies. In a first investigation of LaLuO$_{3}$ on germanium, germanate formation is shown. LaLuO$_{3}$ is further integrated in a high-temperature MOSFET process flow with varying thermal treatment. The devices feature drive currents up to 70µA/µm at 1µm gate length. Several optimization steps are presented. The effective device mobility is related to silicate formation and thermal budget. At high temperature the silicate formation leads to mobility degradation due to La-rich silicate formation. The integration of LaLuO$_{3}$ in high-T processes delicately connects with the optimization of the TiN metal electrode. Hereby, stoichiometric TiN yields the best results in terms of thermal stability with respect to Si-capping and high$\kappa$ oxide. Different approaches are presented for a further EOT reduction with LaLuO$_{3}$ and HfO$_{2}$. Thereby the thermodynamic and kinetic predictions are employed to estimate the behavior on the nanoscale. Based on thermodynamics, excess oxygen in the gate stack, especially in oxidized metal electrodes, is identified to prevent EOT scaling below 1.2 nm. The equivalent oxide thickness of HfO$_{2}$ gate stacks is scalable below 1 nm by the use of thinned interfacial SiO$_{2}$. The prevention of oxygen incorporation into the metal electrode by Si-capping maintains the EOT after high temperature annealing. Redox systems are employed within the gate electrode to decrease the EOT of HfO$_{2}$ gate stacks. A lower limit found was EOT=5 Å for Al doping inside TiN. The doping of TiN on LaLuO$_{3}$ is proven by electron energy loss spectroscopy (EELS) studies to modify the interfacial silicate layer to La-rich silicates or even reduce the layer. The oxide quality in Si/HfO$_{2}$/TiN gate stacks is characterized by charge pumping and carrier mobility measurements on 3d MOSFETs a.k.a. FinFETs. The oxide quality in terms of the number of interface (and oxide) traps on top- and sidewall of FinFETs is compared for three different annealing processes. A high temperature anneal of HfO$_{2}$ improves significantly the oxide quality and mobility. The gate oxide integrity (GOI) of gate stacks below 1 nm EOT is determined by time-dependent dielectric breakdown (TDDB) measurements on FinFETs with HfO$_{2}$/TiN gate stacks. A successful EOT scaling has always to consider the oxide quality and resulting reliability. Degraded oxide quality leads to mobility degradation and earlier soft-breakdown, i.e. leakage current increase.

Keyword(s): Dissertation


Note: RWTH Aachen, Diss., 2013

Contributing Institute(s):
  1. Halbleiter-Nanoelektronik (PGI-9)
  2. JARA-FIT (JARA-FIT)
Research Program(s):
  1. 421 - Frontiers of charge based Electronics (POF2-421) (POF2-421)

Appears in the scientific report 2013
Database coverage:
OpenAccess
Click to display QR Code for this record

The record appears in these collections:
JARA > JARA > JARA-JARA\-FIT
Document types > Theses > Ph.D. Theses
Institute Collections > PGI > PGI-9
Workflow collections > Public records
Publications database
Open Access

 Record created 2013-11-22, last modified 2022-09-30