Experimental Study on the Growth, Coalescence and Wrapping Behaviors of 3D Cross-Embedded Flaws Under Uniaxial Compression

  • Original Paper
  • Published:
Rock Mechanics and Rock Engineering Aims and scope Submit manuscript

Abstract

The crack initiation, growth, wrapping and coalescence of two 3D pre-existing cross-embedded flaws in PMMA specimens under uniaxial compression are investigated. The stress–strain curves of PMMA specimens with 3D cross-embedded flaws are obtained. The tested PMMA specimens exhibit dominant elastic deformation and eventual brittle failure. The experimental results show that four modes of crack initiation and five modes of crack coalescence are observed. The initiations of oblique secondary crack and anti-wing crack in 3D cracking behaviors are first reported as well as the coalescence of anti-wing cracks. Moreover, two types of crack wrapping are found. Substantial wrapping of petal cracks, which includes open and closed modes of wrapping, appears to be the major difference between 2D and 3D cracking behaviors of pre-existing flaws, which are also first reported. Petal crack wraps symmetrically from either the propagated wing cracks or the coalesced wing cracks. Besides, only limited growth of petal cracks is observed, and ultimate failure of specimens is induced by the further growth of the propagated wing crack. The fracture mechanism of the tested PMMA specimens is finally revealed. In addition, the initiation stress and the peak stress versus the geometry of two 3D pre-existing cross-embedded flaws are also investigated in detail.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15
Fig. 16
Fig. 17
Fig. 18
Fig. 19
Fig. 20
Fig. 21
Fig. 22

Similar content being viewed by others

References

  • Bobet A, Einstein HH (1998) Fracture coalescence in rock-type materials under uniaxial and biaxial compression. Int J Rock Mech Min Sci 35(7):863–889

    Article  Google Scholar 

  • Cao P, Liu T, Pu C, Lin H (2015) Crack propagation and coalescence of brittle rock-like specimens with pre-existing cracks in compression. Eng Geol 187:113–121

    Article  Google Scholar 

  • Cheng H, Zhou X, Zhu J, Qian Q (2016) The effects of crack openings on crack initiation, propagation and coalescence behavior in rock-like materials under uniaxial compression. Rock Mech Rock Eng 2016:1–14

    Google Scholar 

  • Dyskin AV, Germanovich LN, Jewell RJ, Joer H, Krasinski JS, Lee KK (1994a) Study of 3D mechanisms of crack growth and interaction in uniaxial compression. ISRM News J 2(1):17–20

    Google Scholar 

  • Dyskin AV, Jewell RJ, Joer H, Sahouryeh E, Ustinov KB (1994b) Experiments on 3D crack growth in uniaxial compression. Int J Fract 65(4):R77–R83

    Article  Google Scholar 

  • Dyskin AV, Sahouryeh E, Jewell RJ, Joer H, Ustinov KB (2003) Influence of shape and locations of initial 3D cracks on their growth in uniaxial compression. Eng Fract Mech 70(15):2115–2136

    Article  Google Scholar 

  • Fu JW, Chen K, Zhu WS, Zhang XZ, Li XJ (2016) Progressive failure of new modelling material with a single internal crack under biaxial compression and the 3-D numerical simulation. Eng Fract Mech 165:140–152

    Article  Google Scholar 

  • Germanovich LN, Dyskin AV (2000) Fracture mechanisms and instability of openings in compression. Int J Rock Mech Min Sci 37:263–284

    Article  Google Scholar 

  • Hoek E, Martin CD (2014) Fracture initiation and propagation in intact rock—a review. J Rock Mech Geotech Eng 6(4):287–300

    Article  Google Scholar 

  • Li H, Wong LNY (2012) Influence of flaw inclination angle and loading condition on crack initiation and propagation. Int J Solids Struct 49(18):2482–2499

    Article  Google Scholar 

  • Park CH, Bobet A (2009) Crack coalescence in specimens with open and closed flaws: a comparison. Int J Rock Mech Min Sci 46(5):819–829

    Article  Google Scholar 

  • Sahouryeh E, Dyskin AV, Germanovich LN (2002) Crack growth under biaxial compression. Eng Fract Mech 69:2187–2198

    Article  Google Scholar 

  • Tang CA, Lin P, Wong RHC, Chau KT (2001) Analysis of crack coalescence in rock-like materials containing three flaws—part II: numerical approach. Int J Rock Mech Min Sci 38(7):925–939

    Article  Google Scholar 

  • Wong LNY, Zhang XP (2014) Size effects on cracking behavior of flaw-containing specimens under compressive loading. Rock Mech Rock Eng 47(5):1921–1930

    Article  Google Scholar 

  • Wong RHC, Chau KT, Tang CA, Lin P (2001) Analysis of crack coalescence in rock-like materials containing three flaws—part I: experimental approach. Int J Rock Mech Min Sci 38(7):909–924

    Article  Google Scholar 

  • Wong RHC, Law CM, Chau KT, Zhu WS (2004) Crack propagation from 3D surface fractures in PMMA and marble samples under uniaxial compression. Int J Rock Mech Min Sci 41(3):1–6

    Article  Google Scholar 

  • Wong RHC, Guo YSH, Li LY, Chau KT, Zhu WS, Li SC (2006) Anti-wing crack growth from surface flaw in real rock. In: Proceedings of the 16th European conference of fracture, Alexandroupolis, pp 825–826

  • Wong RHC, Guo YSH, Liu LQ, Liu PX, Ma SP (2008) Nucleation and growth of anti-wing crack from tips of strike-slip flaw. In: Proceedings of the 42nd US rock mechanics symposium (USRMS), San Francisco, pp 221–229

  • Yang SQ, Jing HH (2013) Evaluation on strength and deformation behavior of red sandstone under simple and complex loading paths. Eng Geol 164:1–17

    Article  Google Scholar 

  • Yang SQ, Liu XR, Jing HW (2013) Experimental investigation on fracture coalescence behavior of red sandstone containing two unparallel fissures under uniaxial compression. Int J Rock Mech Min Sci 63(5):82–92

    Google Scholar 

  • Yang SQ, Tian WL, Huang YH, Ranjith PG, Yu Y (2016) An experimental and numerical study on cracking behavior of brittle sandstone containing two non-coplanar fissures under uniaxial compression. Rock Mech Rock Eng 49(4):1497–1515

    Article  Google Scholar 

  • Yin P, Wong RHC, Chau KT (2014) Coalescence of two parallel pre-existing surface cracks in granite. Int J Rock Mech Min Sci 68(6):66–84

    Google Scholar 

  • Zhou XP, Cheng H, Feng YF (2014) An experimental study of crack coalescence behavior in rock-like materials containing multiple flaws under uniaxial compression. Rock Mech Rock Eng 47(6):1961–1986

    Article  Google Scholar 

  • Zhou XP, Bi J, Qian QH (2015) Numerical simulation of crack growth and coalescence in rock-like materials containing multiple pre-existing flaws. Rock Mech Rock Eng 48(3):1097–1114

    Article  Google Scholar 

  • Zhuang X, Chun J, Zhu H (2014) A comparative study on unfilled and filled crack propagation for rock-like brittle material. Theor Appl Fract Mech 72(1):110–120

    Article  Google Scholar 

Download references

Acknowledgements

This work was supported by Project 973 (Grant No. 2014CB046903) and the National Natural Science Foundation of China (Nos. 51325903 and 51679017).

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Xiao-Ping Zhou.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Zhou, XP., Zhang, JZ. & Wong, L.N.Y. Experimental Study on the Growth, Coalescence and Wrapping Behaviors of 3D Cross-Embedded Flaws Under Uniaxial Compression. Rock Mech Rock Eng 51, 1379–1400 (2018). https://doi.org/10.1007/s00603-018-1406-4

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00603-018-1406-4

Keywords

Navigation