Long-term sulfate resistance of synthesized cement systems with variable C₃A/C₄AF ratio at low temperature or ambient conditions: Insights into the crystalline and amorphous phase assemblage

0559240 - ÚTAM 2023 RIV GB eng J - Článek v odborném periodiku
Sotiriadis, Konstantinos - Mróz, R. - Mácová, Petra - Mazur, A. S. - Krajnc, A.
Long-term sulfate resistance of synthesized cement systems with variable C₃A/C₄AF ratio at low temperature or ambient conditions: Insights into the crystalline and amorphous phase assemblage.
Cement and Concrete Research. Roč. 160, October (2022), č. článku 106902. ISSN 0008-8846. E-ISSN 1873-3948
Grant CEP: GA ČR(CZ) GJ18-26056Y
Institucionální podpora: RVO:68378297
Klíčová slova: sulfate resistance * aluminate phases * carbonation * solid-state NMR spectroscopy * EPR spectroscopy
Obor OECD: Materials engineering
Impakt faktor: 11.4, rok: 2022
Způsob publikování: Open access
https://doi.org/10.1016/j.cemconres.2022.106902

Synthesized cement systems made with variable C₃A/C₄AF ratios, containing C₃S, gypsum and, optionally, calcite, were stored long-term at humid conditions at 5 or 20 °C, without any protection against atmospheric carbonation. Analytical techniques able to assess both the crystalline and amorphous phases were used. Experimental results were compared with thermodynamic simulations. The systems with C₃A/C₄AF < 1 better preserved the soundness of the C–S–H phase, which hosted iron, and prevented thaumasite formation. The addition of calcite in these systems inhibited carbonation. When occurred (mixtures without calcite), the carbonation was significantly more intense at ambient temperature. In the systems that underwent extensive deterioration, cross-linking of silicate structures, AFt decomposition, and iron release from the deteriorating C–S–H, occurred, while Al-incorporating amorphous silica, calcium carbonate polymorphs and hydrous iron oxide formed. The presence of unreacted C₃A in the systems with C₃A/C₄AF = 1, suggested that C–S–H decomposition was contributed by available sulfates.