The effect of treatment of powder precursor on the properties of compacted Mg-4Y-3Re alloy

0578841 - FZÚ 2024 RIV US eng J - Článek v odborném periodiku
Dvorský, Drahomír - Kubásek, J. - Nečas, D. - Čavojský, M. - Drahokoupil, Jan - Vojtěch, D.
The effect of treatment of powder precursor on the properties of compacted Mg-4Y-3Re alloy.
Journal of Engineering Materials and Technology-Transactions of the Asme. Roč. 145, č. 4 (2023), č. článku 045001. ISSN 0094-4289. E-ISSN 1528-8889
Institucionální podpora: RVO:68378271
Klíčová slova: materials processing * mechanical behavior * metals * powder metallurgy * magnesium * extrusion * composites * microstructure property relationships
Obor OECD: Materials engineering
Impakt faktor: 1.2, rok: 2022
Způsob publikování: Omezený přístup
https://doi.org/10.1115/1.4063059

Powder metallurgy products display superior performance compared to traditionally cast ingots. The results show that distinct microstructures were produced, and their impact on mechanical and corrosion properties was evaluated. The results indicate that milling and chemical treatment increase the yield strength of the material by up to 34 MPa but decrease the elongation by up to 5%. On the other hand, heat treatment increases the elongation by up to 7% but decreases the yield strength by up to 36 MPa. Corrosion resistance is improved especially by chemical and heat treatment of powders, where the corrosion rate was observed to decrease by up to 50% in comparison to the value of product from atomized powder. This provides an opportunity to tailor the mechanical and corrosion properties of these materials to meet specific applications.