Show/Hide Menu
Hide/Show Apps
Logout
Türkçe
Türkçe
Search
Search
Login
Login
OpenMETU
OpenMETU
About
About
Open Science Policy
Open Science Policy
Communities & Collections
Communities & Collections
Help
Help
Frequently Asked Questions
Frequently Asked Questions
Guides
Guides
Thesis submission
Thesis submission
MS without thesis term project submission
MS without thesis term project submission
Publication submission with DOI
Publication submission with DOI
Publication submission
Publication submission
Supporting Information
Supporting Information
General Information
General Information
Copyright, Embargo and License
Copyright, Embargo and License
Contact us
Contact us
The effect of Cu and austempering treatment parameters on the impact toughness and hardness of ductile cast iron
Download
035496.pdf
Date
1994
Author
Yaşar, Hakan
Metadata
Show full item record
Item Usage Stats
74
views
0
downloads
Cite This
URI
https://hdl.handle.net/11511/10663
Collections
Graduate School of Natural and Applied Sciences, Thesis
Suggestions
OpenMETU
Core
The effect of austempering parameters on impact and fracture toughness of din 35nicrmov12.5 gun barrel steel
Aksu, Engin; Atala, Haluk; Department of Metallurgical and Materials Engineering (2005)
In this study the effects of different austempering times and temperatures on impact toughness, hardness and fracture toughness properties of 35NiCrMoV12.5 gun barrel steel are investigated. 300 °C, 325 °C and 350 °C were chosen as austempering temperatures. Isothermal holding times at these temperatures were chosen as 1 minute, 10 minutes, 1 hour and 10 hours. It was found that, 350 °C being an exception, austempering temperature and impact toughness has an inverse relationship and impact toughness increas...
The effect of austempering on microstructure and impact toughness of DIN 34CrNiMo5 gun barrel steel
Kurtuluş, B. Murat; Tekin, Erdoğan; Department of Metallurgical Engineering (1994)
The effect of SN content and isothermal transformation temperature on the mechanical properties of austempered ductile cast iron
Özcan, Alper; Atala, Haluk; Department of Metallurgical and Materials Engineering (2003)
In this study the effects of Sn content and isothermal transformation temperature on the ultimate tensile strength (UTS), elongation and hardness of austempered ductile cast iron (ADI) was investigated. To determine the possible effect of Sn on these properties the Sn content of standard GGG30, GGG40 and GGG50 materials were taken as reference, whose chemical compositions vary from 0,016 to 0,050% in terms of Sn. However the Sn content was increased to a maximum of 0,26% for investigating the effect of Sn o...
The effect of initial microstructures prior to hardenening on the wear behavior of SAE 52100 bearing steel
Özbay, Hüseyin Alp; Atala, Haluk; Department of Metallurgical Engineering (1990)
The effect of double austenitization on the microstructure and toughness of AISI M2 high speed steel
Ögel, Bilgehan (1998-06-01)
In this study, the effect of double austenitization on microstructure and toughness of AISI M2 high speed steel was investigated. For double austenitization treatment, the specimens, which are hardened initially at 1220 degrees C and quenched in air, were hardened for a second time in the temperature range 1150 - 1050 degrees C. For comparison purposes, another set of specimens is austenitized singly in the temperature range 1150 - 1050 degrees C. Tempering process was carried out between 500 - 640 degrees ...