The effect of SN content and isothermal transformation temperature on the mechanical properties of austempered ductile cast iron

Download

index.pdf

Date

2003

Author

Özcan, Alper

Metadata

Show full item record

Item Usage Stats

164
views

0
downloads

In this study the effects of Sn content and isothermal transformation temperature on the ultimate tensile strength (UTS), elongation and hardness of austempered ductile cast iron (ADI) was investigated. To determine the possible effect of Sn on these properties the Sn content of standard GGG30, GGG40 and GGG50 materials were taken as reference, whose chemical compositions vary from 0,016 to 0,050% in terms of Sn. However the Sn content was increased to a maximum of 0,26% for investigating the effect of Sn on mechanical properties. The test specimens were obtained from standard 1-in Y-blocks and austenitized at 925oC for 1 hour and austempered at 350oC,375oC, 400oC and 420oC for 60 minutes in a salt bath. Microstructural examination of the specimens were also done. To determine the amount of retained austenite of the specimens X-Ray analyses were used. As a result of the study The UTS increases up to 0,1% Sn and then levels off. A similar behavior is observed in the variation of hardness. Percent elongation decreases and falls to a minimum around 0,1% Sn, from this point on, a slight increase is observed. Strength and hardness increase while percent elongation decreases with decreasing temperatures.

Subject Keywords

Iron, Tin, Materials

URI

http://etd.lib.metu.edu.tr/upload/1055359/index.pdf
https://hdl.handle.net/11511/13731

Collections

Graduate School of Natural and Applied Sciences, Thesis

Suggestions

OpenMETU
Core

The effect of magnisium to sulfur ratio on the graphite morphology of graphite cast iron produced at differrent section thicknesses ELMABROUK, Omar; ERFAN, Osama M.; Kalkanlı, Ali (2011-09-18) This paper is concerned with the investigation of the effect of magnesium to sulfur ratio on the graphite morphology and estimation of the ranges of this ratio use to produce graphite cast iron at different section sections. The main factors affecting shape of graphite cast iron are the metallurgical structures and the section thicknesses. Cast iron of different shapes of graphite particles directly affect its thermo-mechanical properties. The nodular shape of these graphite particles such as in ductile cas...
The synthesis and characterization of aluminum loaded SBA-type materials as catalyst for polypropylene degradation reaction Obali, Zeynep; Sezgi, Naime Aslı; Doğu, Timur (2011-12-01) The performance of pure and aluminum containing SBA-type catalysts prepared using different aluminum sources and different Al/Si ratios were investigated in the polypropylene degradation reaction using a thermogravimetric analyzer. For the synthesis of catalysts, aluminum isopropoxide and aluminum sulphate were used as the aluminum sources. Synthesized materials had high surface areas and exhibited nitrogen adsorption isotherms of type IV. EDS results showed that the aluminum incorporation into the structur...
The effect of triethanolamine on thermal decomposition of GAP Fazhoğlu, Hatice; Hacaloğlu, Jale (2002-01-01) The effect of triethanolamine (TEA) on thermal behavior of glycidyl azide polymer (GAP) has been investigated by direct pyrolysis mass spectrometry technique. It has been observed that thermal degradation of GAP-TEA mixture also begins with the cleavage of the side groups as in the case of GAP. Again, the main decomposition started with the elimination of molecular nitrogen from the azide functional group, and a quite similar degradation mechanism has been proposed. The increase in the thermal stability of ...
Effect of expandable graphite on flame retardant, thermal and mechanical properties of thermoplastic polyurethane composites filled with huntite&hydromagnesite mineral Guler, Turkan; Tayfun, Umit; Bayramlı, Erdal; DOĞAN, Mehmet (2017-01-10) The effect of expandable graphite (EG) was studied on the flame retardant, thermal and mechanical properties of thermoplastic polyurethane (TPU) containing huntite&hydromagnesite (HH). According to the flammability tests results, the synergistic interaction was observed between HH and EG. The maximum limiting oxygen index (LOI value was observed at a ratio of 1:1 (HH:EG) and the highest vertical burning test (UL-94) rating of V0 was observed at a ratios of 4:1, 3:2 and 1:1. The synergistic interaction betwe...
Effect of copper alloying on fatigue life and fatigue crack growth behaviour of ductile cast irons Gürbüz, Rıza; Kalkanlı, Ali (2004-01-01) Specimens cut out and machined from Cu alloyed (about 1.6%) and unalloyed (less than 0.012%) ductile cast iron ingots were tested under cycling loading to reveal the effect of copper addition on fatigue performance. The influence of solidification rate and hence the microstructure were also studied by preparing sand cast and die cast ingots from each composition. Some high copper die cast specimens were annealed to spheroidize and homogenize the matrix's pearlite structure. All experiments were carried out ...

Citation Formats

A. Özcan, “The effect of SN content and isothermal transformation temperature on the mechanical properties of austempered ductile cast iron,” M.S. - Master of Science, Middle East Technical University, 2003.