Microstructural and elecrochemical characterization of Ti-6A1-4V ELI alloy

Download

index.pdf

Date

2006

Author

Topçuoğlu, Melih

Metadata

Show full item record

Item Usage Stats

233
views

92
downloads

In this study, the evolution of structure and the relationship between microstructure and corrosion behavior of the Ti-6Al-4V ELI (Extra Low Interstitial) alloy was investigated in Ringer’s solution at 37 ± 0.1 oC. Initially, different heat treatments were performed in order to obtain several microstructures which were; Widmanstätten α for furnace cooling (FC), basket-weave α for air cooling (AC), martensite (α') for water quenching (WQ) from 1060 oC, and aged martensite for ten hours at 500, 600, 700, 800, 900 oC. The microstructural characterizations were done by using SEM and X-ray Diffraction technique. Finally, the corrosion tests were accomplished in Ringer’s solution and NaF added Ringer’s solution by using open circuit potential and anodic polarization techniques, respectively. The results showed that vanadium element removal from martensite phase and unit cell volume increase were detected during aging due to the replacement of vanadium with titanium atoms. According to the alloying element distribution throughout the microstructure, the passive film formation due to equilibrium corrosion conditions was better in FC specimen than AC and WQ specimens. But during anodic polarization, the stability of the film in high Cl- ion concentration medium was more resistant to dissolution for WQ and aged specimens. As a result, the alloying element distribution underneath the passive film seemed to have an important role on the film formation and its stability. However, in non-equilibrium conditions, the passive film formation tendency due to the addition of NaF at 0.2M decreased because of the detrimental effects of F- ions.

Subject Keywords

Metallurgy.

URI

http://etd.lib.metu.edu.tr/upload/3/12607260/index.pdf
https://hdl.handle.net/11511/15927

Collections

Graduate School of Natural and Applied Sciences, Thesis

Suggestions

OpenMETU
Core

Investigation of fracture behavior of steel/steel laminates Şimşir, Mehmet; Öztürk, Tayfur; Department of Metallurgical and Materials Engineering (2004) A study is carried out into fracture behavior of steel/steel laminates both experimentally and through finite element analysis (FEM). The laminates produced by hot pressing consisted of low carbon and medium carbon steels with two volume fractions; 0.41 and 0.81. Fracture toughness, JIC has been measured using partial unloading technique assuming a critical value of crack extension. The technique is initially applied to monolithic material and then to the laminates in crack divider orientation. Evaluation o...
An investigation of the microstructural and mechanical properties of tri-calcium phosphates doped with aluminum and fluoride ions Tahmasebifar, Aydin; Evis, Zafer; Department of Engineering Sciences (2011) The aim of this study was to investigate the microstructure and mechanical properties of pure tricalcium phosphate (TCP) and tricalcium phosphates doped with aluminum (Al3+) and fluoride (F-) ions at different compositions. TCP was synthesized via precipitation method and sintered at 1100C for 1 and 5 h. It was observed that density and relative density of the sintered materials were decreased by extending the sintering time. Increased densities were achieved upon Al3+ and/or F- doping. For structural anal...
Theoretical and experimental investigation of bulk glass forming ability in bulk amorphous alloy systems Ayas, Can; Mekrabov, Amdulla O.; Department of Metallurgical and Materials Engineering (2005) In this study molecular dynamics simulation program in NVT ensemble using Velocity Verlet integration was written in order to investigate the glass forming ability of two metallic systems. The Zn-Mg system, one of the frontiers of simple metal-metal metallic glasses and Fe-B, inquiring attention due to presence of many bulk glass forming alloy systems evolved from this binary with different alloying element additions. In addition to this, atomistic calculations on the basis of ordering were carried out for ...
Fatigue crack growth behaviour of AA6013 aluminum alloy at different aging conditions Varlı, Aziz Egemen; Gürbüz, Rıza; Department of Metallurgical and Materials Engineering (2006) The effect of different aging treatments on fatigue crack growth behavior of AA6013 aluminum alloy was investigated. C(T) (Compact Tension) specimens were prepared in L-T and T-L direction for fatigue crack growth tests. Samples were in T651 as received, T42 which is solution heat treated at 538 ºC for 90 minutes, water quenched and aged in room temperature for 96 hours, and one group of samples were overaged at 245 ºC for 12 hours after T42 condition was achieved. Hardness and conductivity measurements wer...
Investigation and development of possible leaching processes for recovery of zinc and lead from çinkur leach residues Sunkar, Ahmet Semih; Topkaya, Yavuz Ali; Department of Metallurgical and Materials Engineering (2005) The major aim of this study was to investigate various leaching methods for the recovery of zinc and lead from blended neutral leach residues of Çinkur having a composition of 12.59 % Zn, 15.21 % Pb, 6.45 % Fe, 0.054 % Cd. Initially water leaching tests were performed at various conditions of leaching temperature, reaction time and particle size. The optimized conditions for water leaching were found to be 2 h, 95?C and 250 g/l pulp density with a final pH of 5.9. However, the zinc recovery value of 10.26 %...

Citation Formats

M. Topçuoğlu, “Microstructural and elecrochemical characterization of Ti-6A1-4V ELI alloy,” M.S. - Master of Science, Middle East Technical University, 2006.