Sinter-hardening studies distaloy DH powders with varying carbon contents

Download
index.pdf
2013
Kılıç, Gülten
Show full item record
170
views
122
downloads
In this study, the effect of sinter-hardening on the mechanical properties of Distaloy DH (Fe-2Cu-1.5Mo) powder with 0.4%, 0.6%, and 0,8% graphite additions, was investigated. Powder samples were pressed under 600 MPa, and sintered at 1120°C under endogas from methane for 20 minutes in an industrial sintering furnace. After sintering the samples were cooled with three different cooling rates (0.5°C/sec,1.5°C/sec, and 3°C/sec). Microstructural characterization of samples were done with optical and electron microscopy. Selective etching was utilized in determining the amount of pearlite in samples. The study showed that after sintering, a cooling rate of 0.5°C/s led to decreasing amounts of pearlite in all the Distaloy DH samples with increasing amount of carbon. With increase in the cooling rates to 3°C/s, Distaloy DH-0.4%C sample containis small amount of pearlite, whereas the alloys Distaloy DH–0.6%C and Distaloy DH-0.8%C led to bainitc and martensitic microstructures.
Powder metallurgy., Sintering., Carbon., Sinter (Metallurgy).
http://etd.lib.metu.edu.tr/upload/12616132/index.pdf
https://hdl.handle.net/11511/22681
Graduate School of Natural and Applied Sciences, Thesis

Suggestions

Sinter hardening studies of ASTALOY 85 Mo powder with varying copper contents /
Dinçer, Mehmet; Ögel, Bilgehan; Durlu, Nuri; Department of Metallurgical and Materials Engineering (2014)
In this thesis study, the effect of sinter hardening on mechanical properties of Astaloy 85 Mo (Fe - 0.85% Mo) powder with addition of 0.8% C and varying copper contents (1% Cu, 2% Cu) was examined. Powder mixes were compacted under 600 MPa. After compaction, the samples were sintered at 1120oC under endogas from methane in an industrial sintering furnace and were sinter-hardened with three different cooling rates (0.5oC/sec., 1.5oC/sec., 3oC/sec.). The study revealed that the cooling rate does not make cri...
Processing and characterization of high density tungsten-nickel-iron alloys
Çalışkan, Necmettin Kaan; Bor, Şakir; Durlu, Nuri; Department of Metallurgical and Materials Engineering (2013)
In the present study, processing of W-Ni-Fe alloys by liquid phase sintering technique has been investigated. Effect of sintering atmospheres (hydrogen and vacuum), tungsten content altering from 90 to 97 wt.%, Ni/Fe ratio varied from 2 to 4 and post sintering treatments (heat treatment and swaging) on the microstructure and mechanical properties of W-Ni-Fe alloys have been analyzed. Liquid phase sintered alloys were characterized by mechanical tests, electron microscopy and XRD studies, thermal analyses an...
Mechanical, electrochemical and biocompatibility evaluation of AZ91D magnesium alloy as a biomaterial
Tahmasebifar, Aydin; KAYHAN, Said Murat; Evis, Zafer; Tezcaner, Ayşen; Cinici, Hanifi; Koc, Muammer (2016-12-05)
In this study, the effect of manufacturing conditions (i.e. compaction pressure, sintering temperature and time) on physical, mechanical and electrochemical properties of Mg alloy discs were investigated. The main motivation of this study was to achieve the manufacturing of porous and micro-surface textured Mg-based biomedical implants with good mechanical and electrochemical properties. A Box-Behnken and Full Factorial experimental design was used in experimental investigations. Relative densities of the f...
Production and characterization of porous titanium alloys
Esen, Ziya; Bor, Şakir; Department of Metallurgical and Materials Engineering (2007)
In the present study, production of titanium and Ti6Al4V alloy foams has been investigated using powder metallurgical “space holder technique” in which magnesium powder were utilized to generate porosities in the range 30 to 90 vol. %. Also, sintering of titanium and Ti-6Al-4V alloy powders in loose and compacted condition at various temperatures (850-1250oC) and compaction pressures (120-1125 MPa), respectively, were investigated to elucidate the structure and mechanical properties of the porous cell walls...
Production and characterization of high performance al – fe – v – si alloys for elevated temperature applications
Sayılgan, Seda; Kalkanlı, Ali; Department of Metallurgical and Materials Engineering (2009)
In the present study, the powder metallurgy was evaluated as a technique to produce high performance Al – 8Fe – 1.7V – 7.9Si (wt%) alloys for elevated temperature applications and the role of powder particle size range and extrusion ratio in the microstructural and mechanical properties of the extruded alloys was investigated. For this purpose, an air atomization method was employed to produce powders of the high temperature alloy and after that the produced powders were sieved and cold compacted. The compa...