Effects of SiC particulates on the fatigue behaviour of an Al-alloy matrix composite

Date

2006-01-01

Author

Kaynak, Cevdet

Metadata

Show full item record

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Item Usage Stats

152
views

0
downloads

In this study, the fatigue behaviour of aluminium matrix-silicon carbide (SiC) particulate reinforced composite specimens was investigated in comparison to the matrix aluminium alloy containing 12 wt% Si. Three different weight percentages of SiC particulates: 5, 10, and 15 in the size range of 40-60 gm were injected into the melt. Mg was also added to improve the wettability of Al-alloy matrix over SiC particulates resulting in better interfacial bonding. Test specimens were machined from squeeze casting billets. Hardness, bending and fatigue tests indicated that reinforcing the Al-alloy matrix with SiC particulates improved the hardness, flexural strength and fatigue resistance with increasing content of SiC particulates. Stress levels yielding less than 107 cycles to fracture were applied. Cracks initiated at the debonded particulate-matrix interface and/or by the cracking of the coarse particulates. SiC particulates improved fatigue resistance mainly by acting as barriers to cracks and/or deflecting the growth plane of cracks resulting in decreased crack propagation rates.

Subject Keywords

Metal matrix composites, Fatigue

URI

https://hdl.handle.net/11511/34814

Journal

MATERIALS & DESIGN

DOI

https://doi.org/10.1016/j.matdes.2005.01.009

Collections

Department of Metallurgical and Materials Engineering, Article

Suggestions

OpenMETU
Core

Effect of swaging on microstructure and tensile properties of W-Ni-Fe alloys DURLU, NURİ; Caliskan, N. Kaan; Bor, Sakir (Elsevier BV, 2014-01-01) The objective of this study was to investigate the effect of swaging on the microstructure and tensile properties of high density two phase alloys 90W-7Ni-3Fe and 93W-4.9Ni-2.1Fe. Samples were liquid phase sintered under hydrogen and argon at 1480 degrees C for 30 min and then 15% cold rotary swaged. Measurement of microstructural parameters in the sintered and swaged samples showed that swaging slightly increased tungsten grain size in the longitudinal direction and slightly decreased tungsten grain size i...
Effect of resin and fiber on the abrasion, impact and pressure resistance of cylindrical composite structures Kaya, Derya; Yılmazer, Ülkü; Department of Chemical Engineering (2011) The aim of this study was to investigate the effects of resin and fiber on the abrasion, impact and internal pressure resistances of fiber reinforced plastic composite pipes produced by continuous filament winding method. For this study, pipe samples were produced with different combinations of resin type, fiber type, fiber amount and fiber length. All the samples were tested in accordance with the related ISO (International Organization for Standardization), DIN (German Standardization Institution) and BSI...
Synthesis and characterization of aluminum alloy 7075 reinforced with silicon carbide particulates Kalkanlı, Ali (2008-01-01) In this study 7075 matrix alloy is chosen and SiC particles having average particle size of 29 mu m was incorporated into the alloy at the liquid state before vertical pressure casting. Four different additions of SiCp were made and the weight fractions used are 10%, 15%, 20% and 30%. Composites were processed by vertical pressure/squeeze casting machine developed at Middle East Technical University (METU) under 80 MPa pressure. The mold is specially designed to produce specimens for tensile and three point...
The effect of double austenitization on the microstructure and toughness of AISI M2 high speed steel Ögel, Bilgehan (1998-06-01) In this study, the effect of double austenitization on microstructure and toughness of AISI M2 high speed steel was investigated. For double austenitization treatment, the specimens, which are hardened initially at 1220 degrees C and quenched in air, were hardened for a second time in the temperature range 1150 - 1050 degrees C. For comparison purposes, another set of specimens is austenitized singly in the temperature range 1150 - 1050 degrees C. Tempering process was carried out between 500 - 640 degrees ...
Effects of fabrication method on initial powder characteristics and liquid phase sintering behaviour of tungsten Erol, Mahmut; Erdogan, Metehan; Karakaya, İshak (Elsevier BV, 2018-12-01) Direct electrochemical production of tungsten involves removal of oxygen in solid state from an important tungsten compound, calcium tungstate, in molten salts. A detailed experimental study was performed to characterize the liquid phase sintering behaviour of the tungsten powder (WE), which was produced by the direct electrochemical reduction technique. All of the tungsten heavy alloy (WHA) compositions covered in this study, contained four parts nickel, one part cobalt and over 90 wt% tungsten. The pellet...

Citation Formats

C. Kaynak, “Effects of SiC particulates on the fatigue behaviour of an Al-alloy matrix composite,” MATERIALS & DESIGN, pp. 776–782, 2006, Accessed: 00, 2020. [Online]. Available: https://hdl.handle.net/11511/34814.