Synthesis of calcium carbonate particles for biomedical applications

Download

index.pdf

Date

2020

Author

Oral, Çağatay Mert

Metadata

Show full item record

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Item Usage Stats

371
views

237
downloads

Calcium carbonate (CaCO3) particles have been widely used in biomedical applications owing to their biocompatibility and biodegradability. In order to effectively utilize CaCO3 particles in biomedical applications, their physical and chemical properties should be systematically controlled. However, this is a challenging task due to the presence of three different anhydrous CaCO3 polymorphs having complex crystallization behavior. In this thesis, CaCO3 particles were synthesized at distinct environments to control their properties. By altering temperature and ethylene glycol concentration of the precursor solutions, vaterite or aragonite content of the particles were maximized, while minimizing the average particle size. In addition, pH and [Ca2+]:[CO32-] ratio of the precursor solutions were adjusted to synthesize vaterite and calcite particles having distinct morphologies. By conducting control experiments, ethylene glycol concentration and solution pH were compared for their influence on CaCO3 particle properties. In order to assess the use of synthesized vaterite, aragonite and calcite particles in orthopedic applications, in vitro experiments were conducted using human bone cells. Moreover, an inert gas bubbling method was used to synthesize hollow CaCO3 microspheres for orthopedic applications. Since requirements for the physical and chemical properties of CaCO3 particles are diverse for each biomedical application, the findings of this thesis contributed to identify viable synthesis routes to obtain CaCO3 particles with distinct properties.

Subject Keywords

Biomedical materials., Calcium Carbonate, Biomaterials, Bioceramics, Orthopedics.

URI

http://etd.lib.metu.edu.tr/upload/12625509/index.pdf
https://hdl.handle.net/11511/45725

Collections

Graduate School of Natural and Applied Sciences, Thesis

Suggestions

OpenMETU
Core

Synthesis of calcium carbonate microspheres via inert gas bubbling for orthopedic applications Oral, Cagatay M.; Caliskan, Arda; Goctu, Yagmur; KAPUSUZ, DERYA; Ercan, Batur (Elsevier BV, 2020-02-15) Calcium carbonate (CaCO3) microspheres consisting of vaterite polymorph have been widely used in biomedical applications. Specifically, vaterite microspheres having hollow cores showed significant potential in drug delivery, however the spontaneous transformation of vaterite to other polymorphs in aqueous environments reduced its controlled in vivo release capability. In this work, calcite and aragonite microspheres having hollow/porous inner cores were synthesized -for the first time-using sodium dodecyl s...
Fabrication of functionalized citrus pectin/silk fibroin scaffolds for skin tissue engineering Türkkan, Sibel; Atila, Deniz; Akdağ, Akın; Tezcaner, Ayşen (Wiley, 2018-10-01) In this study, novel porous three-dimensional (3D) scaffolds from silk fibroin (SF) and functionalized (amidated and oxidized) citrus pectin (PEC) were developed for skin tissue engineering applications. Crosslinking was achieved by Schiff's reaction in borax presence as crosslinking coordinating agent and CaCl2 addition. After freeze-drying and methanol treatment, plasma treatment (10 W, 3 min) was applied to remove surface skin layer formed on scaffolds. 3D matrices had high porosity (83%) and interconnec...
Synthesis of biomimetic Ca-hydroxyapatite powders at 37 degrees C in synthetic body fluids Tas, AC (2000-07-01) An important inorganic phase for synthetic bone applications, calcium hydroxyapatite (HA, Ca-10(PO4)(6)(OH)(2)), was prepared as a nano-sized (similar to 50 nm), homogeneous and high-purity ceramic powder from calcium nitrate tetrahydrate and diammonium hydrogen phosphate salts dissolved in modified synthetic body fluid (SBF) solutions at 37 degrees C and pH of 7.4 using a novel chemical precipitation technique. The synthesized precursors were found to easily reach a phase purity >99% after 6 h of calcinati...
Fatigue behavior of TiNi foams processed by the magnesium space holder technique Nakas, G. Ipek; Dericioğlu, Arcan Fehmi; Bor, Sakir (Elsevier BV, 2011-11-01) While the wide range of applications of TiNi alloys makes them highly appealing due to their shape memory and superelasticity properties, the production of TiNi in the porous form further enlarges their application fields. Porous TiNi alloys have been studied extensively for biomedical applications since their elastic modulus is similar to that of bone. Accordingly, TiNi foams have been widely characterized in terms of their various mechanical properties; however, their fatigue properties have not been well...
Synthesis and characterization of multi-hollow opaque polymer pigments Asmaoglu, Serdar; Gündüz, Güngör; MAVİŞ, BORA; Colak, Uner (Wiley, 2016-08-05) A new generation multihollow opaque polymer pigment was synthesized by suspension polymerization of water-in-oil-in-water emulsion method, where methyl methacrylate and ethylene glycol dimethacrylate monomer mixture was used as oil phase. The effects of surfactant and cosurfactant composition in terms of hydrophilic/lipophilic balance on the stability of the water-in-oil emulsion and the size of water droplets were studied. Low droplet sizes and the optimum stability were obtained with Span 80&Tween 80 surf...

Citation Formats

Ç. M. Oral, “Synthesis of calcium carbonate particles for biomedical applications,” Thesis (M.S.) -- Graduate School of Natural and Applied Sciences. Metallurgical and Materials Engineering., Middle East Technical University, 2020.