The use of polyethylene copolymers as compatibilizers in carbon fiber reinforced high density polyethylene composites

Date

2016-08-15

Author

ATABEK SAVAŞ, Lemiye
Tayfun, Umit
DOĞAN, Mehmet

Metadata

Show full item record

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Item Usage Stats

137
views

0
downloads

In the current study, three different commercially available copolymers are used as compatibilizer in carbon fiber (CF) reinforced high density polyethylene (PE) based composites. Polyethylene grafted maleic anhydride (PE-g-MA), a random terpolymer of ethylene, acrylic ester and maleic anhydride (LOT MA) and a random copolymer of ethylene and glycidyl methacrylate (LOT-GMA) are used as compatibilizers. The compatibilizers are used at three concentrations of 1.5, 3 and 6 wt%. The type and amount of compatibilizers on the tensile, impact, flexural, thermomechanical and morphological properties of composites are investigated. The use of coupling agents increases the mechanical properties of composites regardless of their type. The maximum increase in mechanical properties is observed at different concentrations of compatibilizer depending on the test type and compatibilizer type. The effectiveness of the compatibilizers is ranked as follow: LOT-MA > LOT-GMA > PE-g-MA in all mechanical tests. A correlation is observed between the effectiveness of compatibilizers and their polar group content. The higher polar group content causes the higher improvement in mechanical tests studied in this work.

Subject Keywords

Carbon fibre, Thermoplastic resin, Mechanical properties, Thermomechanical, Mechanical testing

URI

https://hdl.handle.net/11511/67088

Journal

COMPOSITES PART B-ENGINEERING

DOI

https://doi.org/10.1016/j.compositesb.2016.06.043

Collections

Department of Chemistry, Article

Suggestions

OpenMETU
Core

Investigating the mechanical properties of single walled carbon nanotube reinforced epoxy composite through finite element modelling Zuberi, Muhammad Jibran Shahzad; Esat, Volkan (2015-03-15) Varying experimental results on the mechanical properties of carbon nanotube reinforced polymer composites (CNTRPs) have been reported due to the complexities associated with the characterization of material properties in nano-scale. Insight into the issues associated with CNTRPs may be brought through computational techniques time- and cost-effectively. In this study, finite element models are generated in which single walled carbon nanotube models are embedded into the epoxy resin. For modelling interface...
The effect of B4C reinforcements on the microstructure, mechanical properties, and wear behavior of AA7075 alloy matrix produced by squeeze casting Demir, Mehmet Emin; ÇELİK, YAHYA HIŞMAN; KILIÇKAP, EROL; Kalkanlı, Ali (2022-11-01) Aluminum and its alloys have become the most popular materials in applications aiming to provide lightness due to their low density. However, the low mechanical properties compared to other competitors are among the disadvantages of aluminum and its alloys. This is an important motivation factor in researching strength increasing mechanisms in aluminum and its alloys. In this study, the effects of reinforcement ratio and type on the microstructure, mechanical properties, and wear behavior of the AA7075/B4C ...
MECHANICAL PROPERTIES OF REPAIRED CARBON FIBER REINFORCED POLYMER COMPOSITES Sonat, Emine Evren; Özerinç, Sezer; Department of Mechanical Engineering (2021-12-10) Carbon fiber reinforced polymer (CFRP) composites are increasingly used in the aerospace industry due to their high specific strength compared to conventional metallic materials. However, a significant shortcoming of these composites is their increased susceptibility to damage. Structural repair is a common method to restore the load-carrying capacity of a damaged part when the damage size exceeds the pre-defined tolerances. Scarf and stepped bonded repair methods are the primary choice for cases that requi...
Process characterization of composite structures manufactured using resin impregnation techniques Miskbay, Adem Onur; Parnas, Kemal Levend; Department of Mechanical Engineering (2009) The aim of this study is to investigate and compare the properties of two layer carbon epoxy composite plates manufactured using various resin impregnation techniques; Resin Transfer Molding (RTM), Light RTM (LRTM), Vacuum Assisted RTM (VARTM) and Vacuum Packaging (VP). Throughout the study a different packaging method was developed and named Modified Vacuum Packaging (BP). The mechanical properties of composite plates manufactured are examined by tensile tests, compressive tests, in-plane shear tests and t...
Development of carbon fabric-reinforced polylactic acid/acrylonitrile butadiene styrene multilayer composites Öztürk, İrem; Bayram, Göknur; Department of Chemical Engineering (2021-8) Multilayer composites are in concern of both world of material science and the industry because of providing enhanced mechanical properties with ultra lightweight. Also, there is a growing demand to use of recyclable, biodegradable materials in polymer composites for the sake of environmental health. In this study, polymer blends were prepared with polylactic acid (PLA) and acrylonitrile butadiene styrene (ABS) with 10, 30, and 50 wt.%. To compatibilize these polymers, styrene-ethylene-butylene-styrene ter...

Citation Formats

L. ATABEK SAVAŞ, U. Tayfun, and M. DOĞAN, “The use of polyethylene copolymers as compatibilizers in carbon fiber reinforced high density polyethylene composites,” COMPOSITES PART B-ENGINEERING, pp. 188–195, 2016, Accessed: 00, 2020. [Online]. Available: https://hdl.handle.net/11511/67088.