Radiation response of alloy T91 at damage levels up to 1000 peak dpa

Date

2016-12-01

Author

Gigax, J. G.
Chen, T.
Kim, Hyosim
Wang, J.
Price, L. M.
Aydoğan Güngör, Eda
Maloy, S. A.
Schreiber, D. K.
Toloczko, M. B.
Garner, F. A.
Shao, Lin

Metadata

Show full item record

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Item Usage Stats

93
views

0
downloads

Ferritic/martensitic alloys are required for advanced reactor components to survive 500-600 neutron-induced dpa. Ion-induced void swelling of ferritic/martensitic alloy T91 in the quenched and tempered condition has been studied using a defocused, non-rastered 3.5 MeV Fe-ion beam at 475 degrees C to produce damage levels up to 1000 peak displacements per atom (dpa). The high peak damage level of 1000 dpa is required to reach 500-600 dpa level due to injected interstitial suppression of void nucleation in the peak dpa region, requiring data extraction closer to the surface at lower dpa levels. At a relatively low peak damage level of 250 dpa, voids began to develop, appearing first in the near-surface region. With increasing ion fluence, swelling was observed deeper in the specimen, but remained completely suppressed in the back half of the ion range, even at 1000 peak dpa. The local differences in dpa rate in the front half of the ion range induce an "internal temperature shift" that strongly influences the onset of swelling, with shorter transient regimes resulting from lower dpa rates, in agreement not only with observations in neutron irradiation studies but also in various ion irradiations. Swelling was accompanied by radiation-induced precipitation of Cu-rich and Si, Ni, Mn-rich phases were observed by atom probe tomography, indicating concurrent microchemical evolution was in progress. In comparison to other ferritic/martensitic alloys during ion irradiation, T91 exhibits good swelling resistance with a swelling incubation period of about 400 local dpa. (C) 2016 Elsevier B.V. All rights reserved.

URI

https://hdl.handle.net/11511/69892

Journal

JOURNAL OF NUCLEAR MATERIALS

DOI

https://doi.org/10.1016/j.jnucmat.2016.10.003

Collections

Department of Metallurgical and Materials Engineering, Article

Suggestions

OpenMETU
Core

Radiation Damage Studies for Fe-Based Alloys Under 30 MeV Proton Irradiation Uslu, Pelin; Akdeniz, Mahmut Vedat; Mehrabov, Amdulla; Demirköz, Melahat Bilge (2019-10-07) Materials should be radiation resistant for safe and reliable operation in radiation environments. Therefore, radiation tests are crucial for new candidate materials. Proton tests are critical for materials intended for use in nuclear reactors that produce hydrogen and hydrogen isotope ions and in the space environment that consists mostly of protons. Generally, crystalline materials are used in nuclear reactors and in space for their mechanical rob...
Nanohardness measurements of heavy ion irradiated coarse- and nanocrystalline-grained tungsten at room and high temperature El-Atwani, O.; Weaver, J. S.; Esquivel, E.; Efe, Mert; Chancey, M. R.; Wang, Y. Q.; Maloy, S. A.; Mara, N. (Elsevier BV, 2018-10-01) Heavy ion irradiation was performed on coarse and nanocrystalline-grained tungsten (CGW and NGW, respectively) at room temperature (RT) and 1050 K from 0.25 to 4 dpa to simulate radiation damage for fusion energy applications. TEM and nanohardness measurements of irradiated samples were made to quantify the radiation tolerance of these two candidate materials. In this case, TEM is used to quantify the defect morphology at low dpa values and determine the barrier strength coefficients of the different defect...
Electrical transport in metal oxide semiconductor capacitors Arıkan, Mustafa; Turan, Raşit; Department of Physics (2004) The current transport mechanisms in metal-oxide-semiconductor (MOS) capacitors have been studied. The devices used in this study have characterized by current-voltage analyses. Physical parameter extractions and computer generated fit methods have been applied to experimental data. Two devices have been investigated: A relatively thick oxide (125 nm) and an ultra-thin oxide (3 nm) MOS structures. The voltage and temperature dependence of these devices have been explained by using present current transport m...
Particle Velocity, Solids Hold-Up, and Solids Flux Distributions in Conical Spouted Beds Operating with Heavy Particles Külah, Görkem; KÖKSAL, MURAT (American Chemical Society (ACS), 2016-03-23) Conical spouted beds operating with high density particles have recently gained attention because of their potential use as nuclear fuel coaters for next-generation nuclear reactors. To design, scale-up, and manufacture these coaters, detailed investigation of local flow structure is of paramount importance. Therefore, in this study, local instantaneous particle velocity and solids hold-up and flux measurements were carried out in spouted beds having a wide range of cone angles (30, 45, 60) using zirconia p...
Passivation of type II InAs/GaSb superlattice photodetectors with atomic layer deposited Al2O3 Salihoglu, Omer; Muti, Abdullah; Kutluer, Kutlu; Tansel, Tunay; Turan, Raşit; KOCABAŞ, COŞKUN; AYDINLI, ATİLLA (2012-04-27) We have achieved significant improvement in the electrical performance of the InAs/GaSb midwave infrared photodetector (MWIR) by using atomic layer deposited (ALD) aluminium oxide (Al2O3) as a passivation layer. Plasma free and low operation temperature with uniform coating of ALD technique leads to a conformal and defect free coverage on the side walls. This conformal coverage of rough surfaces also satisfies dangling bonds more efficiently while eliminating metal oxides in a self cleaning process of the A...

Citation Formats

J. G. Gigax et al., “Radiation response of alloy T91 at damage levels up to 1000 peak dpa,” JOURNAL OF NUCLEAR MATERIALS, pp. 257–265, 2016, Accessed: 00, 2021. [Online]. Available: https://hdl.handle.net/11511/69892.