Processing optimization of SiO2-capped aluminum-doped ZnO thin films for transparent heater and near-infrared reflecting applications

Date

2021-01-01

Author

Can, Hilal Aybike
Tonbul, Beyza
PİŞKİN, FATİH
Öztürk, Tayfur
AKYILDIZ, HASAN

Metadata

Show full item record

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Item Usage Stats

161
views

0
downloads

In this study, a series of optimization steps were performed in the production of Al-doped ZnO (AZO) thin films to tailor their properties as efficient transparent heaters and for near-infrared (NIR) reflectance. The films were produced on 50 x 75 mm(2) glass substrates via magnetron sputtering and capped with a protective SiO2 layer. Processing parameters such as deposition temperature, film thickness, and annealing conditions were all optimized in terms of structure, morphology, optical/electrical properties, and heating/deicing behavior. Electro-thermal characteristics of the films were investigated using a thermal imaging infrared camera under various input voltages. The optimized AZO/SiO2 coatings displayed impressive room-temperature electrical conductivity (sigma) of nearly 3774 S/cm with a sheet resistance (R-s) of 3.53 Omega/square, carrier concentration (eta) of 1.14 x 10(21), and Hall mobility (mu) of 20.48 cm(2)/Vs. These films exhibited very high optical transmittance (above 96%) in the visible range and reflectance (73% at 2500 nm) in the NIR region. The highest figure of merit (FOM) was achieved as 237 (x 10(-3) omega(-1)). Deicing tests were performed with samples cooled to - 40 degrees C and resulted with complete removal of ice/water only within 3 min. In addition, the heater exhibited a high surface temperature of 161 degrees C (12 V), a good thermal resistance value (219 degrees C cm(2)/Watts) with stable and reversible heating behavior. More importantly, these results reveal the potential of optimized AZO/SiO2 coatings as alternatives to transparent tin-doped indium oxide heaters and NIR reflecting mirrors for vehicular applications.

URI

https://hdl.handle.net/11511/89161

Journal

JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS

DOI

https://doi.org/10.1007/s10854-021-05245-6

Collections

Graduate School of Natural and Applied Sciences, Article

Suggestions

OpenMETU
Core

Processing optimization of SiO2-capped aluminum-doped ZnO and amorphous In-Zn-Sn-Oxide thin films for transparent heater and near-infrared reflecting applications Can, Hilal Aybike; Öztürk, Tayfur; Akyıldız, Hasan; Department of Metallurgical and Materials Engineering (2022-2-09) In this study, AZO/SiO2 and amorphous In-Zn-Sn-oxide (a-ZITO) functional coatings were developed with combinatorial approach for transparent heater and heat reflecting applications. AZO/SiO2 and amorphous In-Zn-Sn-oxide (a-ZITO) coatings were obtained via magnetron sputtering. A series of optimization steps were carried out specific to each method and coating type. The samples were produced on 75x50 mm2 glass substrates. Further, optimum post-deposition annealing conditions were identified as 400 °C and Ar+...
Solution processed aluminum-doped ZnO thin films for transparent heater applications Tonbul, Beyza; Can, Hilal; Öztürk, Tayfur; Akyıldız, Hasan (2021-06-01) A study was carried out to tailor the properties of ultrasonic spray pyrolysis deposited Al-doped ZnO (AZO) thin films suitable for transparent heater applications. For this purpose, the influences of solvent/precursor type and molarity, Al-doping concentration, nozzle to substrate distance, solution flow rate, carrier gas flow, substrate temperature, and post-deposition annealing on the microstructure, electrical, optical properties, and heating/ deicing behaviors of the films were investigated. The optimi...
Microporous vanadosilicate films with tailorable V4+/V5+ ratio to achieve enhanced visible-light photocatalysis Kuzyaka, Duygu; Uzun, Ceren; Yıldız, İlker; Kaya, Murat; Akata Kurç, Burcu (2021-08-01) This study investigates the changes induced into the photocatalytic activity under solar light irradiation upon changing the structural film properties and tailor the concentration of defects in microporous vanadosilicate AM-6 films. For this purpose, the preparation of AM-6 films with different V4+/V5+ ratios and their utilization as photocatalysts for the decomposition of MB were carried out. Two approaches were used for obtaining AM-6 films with different V4+/V5+ ratios: altering the seed layer coating t...
Annealing Effect on Dark Electrical Conductivity and Photoconductivity of Ga-In-Se Thin Films IŞIK, MEHMET; Güllü, Hasan Hüseyin (2018-05-01) Dark-conductivity and photoconductivity properties of thermally evaporated Ga-In-Se (GIS) thin films were investigated in the temperature range of 80-430 K. All measurements were performed on as-grown and annealed GIS thin films at 300 and 400 degrees C to get information about the effect of the annealing temperature on the conductivity properties. Room temperature conductivity was obtained as 1.8 x 10(-8) Omega(-1) cm(-1) for as-grown films and increased to 3.6 x 10(-4) Omega(-1) cm(-1) for annealed films ...
Processing and assessment of aluminum ceramic fiber reinforced aluminum metal matrix composite parts for automotive and defense applications Türkyılmaz, Gökhan; Kalkanlı, Ali; Department of Metallurgical and Materials Engineering (2009) The aim of this study was to produce partially reinforced aluminum metal matrix composite components by insertion casting technique and to determine the effects of silicon content, fiber vol% and infiltration temperature on the mechanical properties of inserts, which were the local reinforcement parts of the components. Silicon content of alloys was selected as 7 wt% and 10 wt%. The reinforcement material, i.e. Saffil fiber preforms, had three different fiber vol% of 20, 25 and 30 vol% respectively. The inf...

Citation Formats

H. A. Can, B. Tonbul, F. PİŞKİN, T. Öztürk, and H. AKYILDIZ, “Processing optimization of SiO2-capped aluminum-doped ZnO thin films for transparent heater and near-infrared reflecting applications,” JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, pp. 0–0, 2021, Accessed: 00, 2021. [Online]. Available: https://hdl.handle.net/11511/89161.