Experimental investigation of failure mechanism in cross-ply and fabric curved composite laminates

Download

index.pdf

Date

2021-8

Author

Çevik, Ahmet

Metadata

Show full item record

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Item Usage Stats

255
views

228
downloads

Laminated curved-shape composite parts which are used in the spar and ribs in aircraft and wind turbine blades are subjected to high interlaminar tensile and shear stresses. These stresses cause delamination and subsequent reduction in load-carrying capacity. In this study, failure mechanism of cross-ply and fabric curved composite laminates under pure transverse loading are examined experimentally using an in-house designed test fixture. Stress field over the curved beam is obtained with finite element analyses (FEA) and analytic solution where multilayered theory is used. Dynamic delamination of the cross-ply and fabric curved specimens is recorded with a high-speed camera where the failure sequence is captured and the crack tip speeds are calculated. For the cross-ply laminates, von Mises strain field is obtained with digital image correlation (DIC) method where the strain fields are found to agree well with elastic FEA up to a specific loading at which a population of matrix cracks nucleate. Detailed fractography of the tested specimens is carried out with digital microscope. Finite element analysis with 2D Hashin Failure criteria is also successfully predict the radial cracks observed in the micrographs of cross-ply curved composite laminates. However, the meandering crack path could not be properly predicted with 2D Hashin Failure Criteria. In fabric curved composite laminates, the failure is observed to occur due to inter-ply and intra-ply crack growth. In fabric laminates, the crack tip travels in a fluctuating manner at speeds reaching intersonic speeds whereas in cross-ply laminates the crack tip speed reaches about Rayleigh wave speed.

Subject Keywords

Curved composite, Delamination, Failure mechanism, Fractography, Crack tip speed

URI

https://hdl.handle.net/11511/92928

Collections

Graduate School of Natural and Applied Sciences, Thesis

Suggestions

OpenMETU
Core

Experimental Observations of Dynamic Delamination in Curved [0] and [0/90] Composite Laminates Imren, Uyar; Miray, Arca; Burak, Gozluklu; Çöker, Demirkan (null, Springer, 2015-01-01) Curved composite parts are increasingly replacing metal ribs and box structures in recent civil aerospace structures and wind turbine blades. Delamination of L-shaped composite laminates occurs by interlaminar opening stresses in addition to the interlaminar shear stresses at the curved region. An experimental setup is designed to investigate dynamic delamination in L-shaped composite brackets under quasi static shear loading. The materials are unidirectional [0]17and cross-ply [0/90]17 epoxy/graphite compo...
Experimental Observations of Dynamic Delamination in Curved [0] and [0/90] Composite Laminates Uyar, I.; Arca, M.A.; Gozluklu, B.; Çöker, Demirkan (2015-01-01) Curved composite parts are increasingly replacing metal ribs and box structures in recent civil aerospace structures and wind turbine blades. Delamination of L-shaped composite laminates occurs by interlaminar opening stresses in addition to the interlaminar shear stresses at the curved region. An experimental setup is designed to investigate dynamic delamination in L-shaped composite brackets under quasi static shear loading. The materials are unidirectional [0]17and cross-ply [0/90]17 epoxy/graphite compo...
Numerical modeling of failure in composite L-beam and T-joint structures Temiz, Pakize; Çöker, Demirkan; Department of Aerospace Engineering (2022-12-02) Laminated curved-shape composite structures which are used as stiffening components in aerospace, wind, automotive and marine industries are subjected to high radial and tangential stresses. For the scope of this thesis, different modelling strategies are investigated to simulate interlaminar and intralaminar failure in composite L-beam and T-joint structures using commercial finite element (FE) code ABAQUS/Standard 2020. In the first part, [030] and [03/903/03/903/03]s laminated L-beams are evaluated using...
Delamination-Debond Behaviour of Composite T-Joints in Wind Turbine Blades Gulasik, H.; Çöker, Demirkan (2014-06-20) Wind turbine industry utilizes composite materials in turbine blade structural designs because of their high strength/stiffness to weight ratio. T-joint is one of the design configurations of composite wind turbine blades. T-joints consist of a skin panel and a stiffener co-bonded or co-cured together with a filler material between them. T-joints are prone to delaminations between skin/stiffener plies and debonds between skin-stiffener-filler interfaces. In this study, delamination/debond behavior of a co-b...
Experimental Investigation of Strength of Curved Beam by Thin Ply Non-Crimp Fabric Laminates Arca, M. A.; PAPİLA, MELİH; Çöker, Demirkan (2016-06-09) Resistance against delamination failure and through the thickness tensile properties of curved carbon fiber reinforced plastics composites are investigated experimentally by conducting the curved beam strength tests. Effect of novel material thin ply non crimp fabric (NCF) architecture on delamination resistance of carbon fiber reinforced composites are investigated and compare with that of standard UD layups. In order to determine through the thickness tensile properties of curved carbon fiber composites, ...

Citation Formats

A. Çevik, “Experimental investigation of failure mechanism in cross-ply and fabric curved composite laminates,” M.S. - Master of Science, Middle East Technical University, 2021.