Título: | Mobility and glass transition temperature of polymer nanospheres |
Autor: | Zhang, Chuan; Boucher, Virginie M. CSIC ORCID; Cangialosi, Daniele CSIC ORCID ; Priestley, Rodney D. | Fecha de publicación: | 2013 | Editor: | Elsevier | Citación: | Polymer 54(1): 230-235 (2013) | Resumen: | Recent studies have illustrated a decoupling between cooperative segmental mobility and the glass transition temperature (Tg) of thin polymer films and nanocomposites. Here, we use dielectric spectroscopy to probe the cooperative segmental mobility and capacitive dilatometry to determine the Tg of films of polystyrene nanospheres with diameters (d) less than 400 nm. We find that both capacitive dilatometry and calorimetry revealed nearly identical suppressions in Tg as the size of the nanospheres was reduced. While Tg was impacted by confinement, in the range 130 nm ≤ d ≤ 400 nm, in stark contrast, the cooperative segmental mobility, i.e., the peak position of the α-relaxation process was not. Furthermore, when d ≤ 200 nm, an additional molecular relaxation process, not observed in bulk, was present. We interpret these findings as evidence of a decoupling between Tg and cooperative segmental mobility in nanospheres. That is, the latter may be impacted by confinement under conditions in which the former is not. | URI: | http://hdl.handle.net/10261/102535 | DOI: | 10.1016/j.polymer.2012.11.036 | Identificadores: | doi: 10.1016/j.polymer.2012.11.036 issn: 0032-3861 |
Aparece en las colecciones: | (CFM) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
accesoRestringido.pdf | 15,38 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
60
checked on 20-abr-2024
WEB OF SCIENCETM
Citations
56
checked on 24-feb-2024
Page view(s)
443
checked on 24-abr-2024
Download(s)
102
checked on 24-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.