Título: | Palladium supported on porous chitosan-graphene oxide aerogels as highly effcient catalysts for hydrogen generation from formate |
Autor: | Anouar, A.; Katir, N.; El Kadib, A.; Primo, Ana CSIC ORCID; García Gómez, Hermenegildo CSIC ORCID CVN | Fecha de publicación: | 10-sep-2019 | Editor: | Molecular Diversity Preservation International | Citación: | Molecules 24(18): 3290 (2019) | Resumen: | Adsorption of Pd(NH) in preformed chitosan-graphene oxide (CS-GO) beads and their subsequent reduction with NaBH afford well-dispersed, high dispersion (∼21%) of uniformly sized Pd nanoparticles (∼1.7 nm). The resulting Pd/CS-GO exhibits interesting catalytic activity for hydrogen generation by ammonium formate decomposition. The optimal GO proportion of 7 wt% allows reaching, at 60 °C, a turnover frequency above 2200 h-being outstanding among the highest values reported for this process to date. Interestingly, no formation of CO or CH was detected. The catalyst did not leach, although it underwent gradual deactivation, probably caused by the increase in the Pd average size that became over 3 nm after three uses. Our results are relevant in the context of efficient on-board hydrogen generation from liquid organic hydrogen carriers in transportation. | Versión del editor: | http://dx.doi.org/10.3390/molecules24183290 | URI: | http://hdl.handle.net/10261/207874 | DOI: | 10.3390/molecules24183290 | Identificadores: | doi: 10.3390/molecules24183290 issn: 1420-3049 |
Aparece en las colecciones: | (ITQ) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
Palladium Supported on Porous... molecules-24-03290.pdf | 10,71 MB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
PubMed Central
Citations
6
checked on 10-abr-2024
SCOPUSTM
Citations
19
checked on 25-abr-2024
WEB OF SCIENCETM
Citations
19
checked on 25-feb-2024
Page view(s)
91
checked on 26-abr-2024
Download(s)
96
checked on 26-abr-2024