Synthesis, Superstructure, and Vacancy-Ordering in 2H-CuxTa1+ySe2 (x, y = 0.52, 
0 and 0.16, 0.08)

Ali, Sk Imran; Mondal, Swastik; van Smaalen, Sander

doi:10.1002/zaac.201400335

アイテム詳細

登録内容を編集ファイル形式で保存

一時保存へ追加

タグ情報を表示リリース履歴を表示詳細要約

公開

学術論文

Synthesis, Superstructure, and Vacancy-Ordering in 2H-Cu_xTa_1+ySe₂ (x, y = 0.52, 0 and 0.16, 0.08)

MPS-Authors

/persons/resource/persons179834

Mondal, Swastik
Laboratory of Crystallography, University of Bayreuth;
Service Department Lehmann (EMR), Max-Planck-Institut für Kohlenforschung, Max Planck Society;

External Resource

There are no locators available

Fulltext (restricted access)

There are currently no full texts shared for your IP range.

フルテキスト (公開)

公開されているフルテキストはありません

付随資料 (公開)

There is no public supplementary material available

引用

Ali, S. I., Mondal, S., & van Smaalen, S. (2015). Synthesis, Superstructure, and Vacancy-Ordering in 2H-Cu_xTa_1+ySe₂ (x, y = 0.52, 0 and 0.16, 0.08). Zeitschrift für anorganische und allgemeine Chemie, 641(2), 464-469. doi:10.1002/zaac.201400335.

引用: https://hdl.handle.net/11858/00-001M-0000-0027-C14F-E

要旨

Single crystals of Cu_xTa_1+ySe₂ were grown by chemical vapor transport. Single crystals of different compositions were obtained at slightly different reaction conditions from mixtures of the reactants of the same nominal composition. It is suggested that different diameters of the ampoules imply different contributions of convection and diffusion to the mass transport, and thus are responsible for different ratios of the amount of Cu, Ta, and Se transported. 2H-Cu_0.52TaSe₂ (x = 0.52, y = 0) is formed in the narrower ampoule (diameter 15 mm). The crystal structure is based on the MoS₂ type of stacking of TaSe₂ layers. Partial ordering of Cu over the tetrahedral sites is responsible for a 2a₀ X 2b₀ X c₀ superstructure with hexagonal P6̅m2 symmetry [a₀ = 3.468 (1) Å, c₀ = 13.568 (3) Å]. 2HCu_0.16Ta_1.08Se₂ (x = 0.16, y = 0.08) is formed in the wider ampoule (diameter 18 mm). It possesses a NbS₂-type of stacking. A superstructure is not formed, but the presence of Cu and intercalated Ta in alternating van der Waals gaps is responsible for the reduction of symmetry from P6₃/mmc to P3̅m1 [a₀ = 3.439 (2) Å, c₀ = 12.870 (2) Å]. Single crystals are formed towards the hotter side of the ampoules up to a temperature of 1168 K in both reactions.