Microstructure evolution and sintering kinetics of ZnO
Апстракт
The aim of this work was to analyse the kinetics and microstructure evolution of ZnO sintering process. ZnO powder was isothermally sintered (15, 30, 60, 90 and 120 min) in the temperature range from 8000C to 12000C. The values of Lenel parameter were calculated and used for the analysis of the densification and mass transport processes. Using scanning electron microscopy the analysis of the microstructure evolution and dependence of the average grain size with temperature and time of sintering was obtained. The results of this research could enable development of a new phenomenological equations in the analyses of ZnO-based materials sintering kinetics.
Кључне речи:
Kinetics / Sintering / ZnOИзвор:
Journal of Applied Engineering Science, 2011, 9, 2, 317-322Издавач:
- Institut za istraživanja i projektovanja u privredi, Beograd
Институција/група
Poljoprivredni fakultetTY - JOUR AU - Kosanović, Darko AU - Filipović, Suzana AU - Obradović, N. AU - Pavlović, Vladimir AU - Ristić, M. PY - 2011 UR - http://aspace.agrif.bg.ac.rs/handle/123456789/2437 AB - The aim of this work was to analyse the kinetics and microstructure evolution of ZnO sintering process. ZnO powder was isothermally sintered (15, 30, 60, 90 and 120 min) in the temperature range from 8000C to 12000C. The values of Lenel parameter were calculated and used for the analysis of the densification and mass transport processes. Using scanning electron microscopy the analysis of the microstructure evolution and dependence of the average grain size with temperature and time of sintering was obtained. The results of this research could enable development of a new phenomenological equations in the analyses of ZnO-based materials sintering kinetics. PB - Institut za istraživanja i projektovanja u privredi, Beograd T2 - Journal of Applied Engineering Science T1 - Microstructure evolution and sintering kinetics of ZnO EP - 322 IS - 2 SP - 317 VL - 9 UR - https://hdl.handle.net/21.15107/rcub_agrospace_2437 ER -
@article{ author = "Kosanović, Darko and Filipović, Suzana and Obradović, N. and Pavlović, Vladimir and Ristić, M.", year = "2011", abstract = "The aim of this work was to analyse the kinetics and microstructure evolution of ZnO sintering process. ZnO powder was isothermally sintered (15, 30, 60, 90 and 120 min) in the temperature range from 8000C to 12000C. The values of Lenel parameter were calculated and used for the analysis of the densification and mass transport processes. Using scanning electron microscopy the analysis of the microstructure evolution and dependence of the average grain size with temperature and time of sintering was obtained. The results of this research could enable development of a new phenomenological equations in the analyses of ZnO-based materials sintering kinetics.", publisher = "Institut za istraživanja i projektovanja u privredi, Beograd", journal = "Journal of Applied Engineering Science", title = "Microstructure evolution and sintering kinetics of ZnO", pages = "322-317", number = "2", volume = "9", url = "https://hdl.handle.net/21.15107/rcub_agrospace_2437" }
Kosanović, D., Filipović, S., Obradović, N., Pavlović, V.,& Ristić, M.. (2011). Microstructure evolution and sintering kinetics of ZnO. in Journal of Applied Engineering Science Institut za istraživanja i projektovanja u privredi, Beograd., 9(2), 317-322. https://hdl.handle.net/21.15107/rcub_agrospace_2437
Kosanović D, Filipović S, Obradović N, Pavlović V, Ristić M. Microstructure evolution and sintering kinetics of ZnO. in Journal of Applied Engineering Science. 2011;9(2):317-322. https://hdl.handle.net/21.15107/rcub_agrospace_2437 .
Kosanović, Darko, Filipović, Suzana, Obradović, N., Pavlović, Vladimir, Ristić, M., "Microstructure evolution and sintering kinetics of ZnO" in Journal of Applied Engineering Science, 9, no. 2 (2011):317-322, https://hdl.handle.net/21.15107/rcub_agrospace_2437 .